牌号简介 About |
---|
Vydyne® R530H NAT是通用的,热稳定,抗水解,30%玻璃纤维增强PA66树脂。天然的,它是专门设计的,以最大限度地保留物理性质时,暴露在抗冻溶液在高温下。该产品也经过润滑以改善机器的进料和流量。与未增强的PA66相比,玻璃增强的Vydyne树脂具有更高的热变形温度、抗蠕变和更好的尺寸稳定性。这些产品对包括汽油、液压油和大多数溶剂在内的各种化学品具有良好的耐化学性。Vydyne® R530H NAT是热稳定的,以最大限度地减少聚合物在使用中暴露于高温下的氧化降解。该产品在长期高温下可提高物理性能的保持力。此外,Vydyne® R530H NAT还具有优异的编织线强度和抗疲劳性能,这对于使用防冻液进行循环测试至关重要。典型应用/最终用途:Vydyne® R530H NAT已用于几种发动机罩下的汽车应用。抗水解性能使其成为散热器端部水箱和加热器芯应用的理想选择。 Vydyne R530H NAT is general-purpose, heat-stabilized, hydrolysis-resistant, 30% glass-fiber reinforced PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is also lubricated for improved machine feed and flow. Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents. Vydyne R530H NAT is heat-stabilized to minimize oxidative degradation of the polymer when exposed to elevated temperatures in service. This product provides improved retention of physical properties under exposure to long-term heat. Also, Vydyne R530H NAT has excellent knit-line strength and fatigue resistance, which is essential for cycle testing with anti-freeze solutions. Typical Applications/End Uses: Vydyne R530H NAT has been used for several under-the-hood automotive applications. The hydrolysis-resistant properties make it an excellent candidate for radiator end tank and heater core applications. |
产品描述 Product Description
厂家:美国奥升德 Ascend
类别:PA66 PA66
用途:汽车的发动机罩下的零件;
颜色:自然色
加工条件:注射成型 Injection Molding
性能特点: 防火阻燃等级HB; 热稳定性好; 耐汽油; 耐疲劳性好; 耐化学性; 耐低温; 润滑性; 耐水解; 易流动; Hydrolysis stability,Good liquidity,Antifreeze,Lubricating,Fatigue resistance,Solvent resistance,Gasoline resistance,Heat Stabilized,HB
填料:玻璃纤维 30
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.37 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:23℃,2.0 mm TD:23℃,2.0 mm |
0.90 | % | ISO 294-4 |
MD:23℃,2.0 mm MD:23℃,2.0 mm |
0.40 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
平衡,50% RH Balance, 50% RH |
1.9 | % | ISO 62 |
23℃,24hr 23℃,24hr |
0.90 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
泊松比 Poisson's ratio |
|||
23℃ 23℃ |
ISO 527 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180 | ||
-30℃ -30℃ |
kJ/m² | ISO 180 | |
23℃ 23℃ |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃,2 mm TD:23~55℃,2 mm |
1/℃ | ISO 11359-2 | |
MD:23~55℃,2 mm MD:23~55℃,2 mm |
1/℃ | ISO 11359-2 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
3.0 mm 3.0 mm |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
1 mm 1 mm |
kV/mm | IEC 60243 | |
耐电弧性 Arc resistance |
|||
3.0 mm 3.0 mm |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
3.00 mm 3.00 mm |
V | IEC 60112 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
0.75 mm 0.75 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
0.75 mm 0.75 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
投资37.5亿元!鲁南化工30万吨己内酰胺项目两套装置中交
2021-07-29 搜料网资讯: 7月25日,由十六化建第五分公司承建的兖矿鲁南30万吨/年己内酰胺项目双氧水装置及硫酸装置迎来重要节点,双氧水及硫酸装置顺利完成中交。该项目的中交标志着两套装 |
投资37.5亿元!鲁南化工30万吨己内酰胺项目两套装置中交 搜料网资讯:7月25日,由十六化建第五分公司承建的兖矿鲁南30万吨/年己内酰胺项目双氧水装置及硫酸装置迎来重要节点,双氧水及硫酸装置顺利完成中交。该项目的中交标志着两套装置全面进入投料开车阶段。 据悉,兖矿鲁南化工有限公司30万吨/年己内酰胺项目配套32万吨/年双氧水装置及40万吨/年硫酸装置,自五月以来经过开车前安全评审“三查四定”检查验收,顺利完成中交节点。
兖矿鲁南化工有限公司30万吨/年己内酰胺项目总投资约为37.55亿元,位于鲁南高科技化工园区兖矿鲁南化工有限公司院内。建设一套年产27万吨环己酮和30万吨己内酰胺同时副产6万吨环己烷和40万吨硫酸铵装置及配套辅助装置,是山东省新旧动能转换重点项目。工艺装置主要为环己酮装置、己内酰胺装置(包含氨肟化装置、液相重排装置、中和结晶装置)、双氧水装置、硫酸装置(其中环己酮装置为单条线,单线生产能力27 万吨/年;双氧水装置为单条线,单线生产能力40万吨/年;硫酸装置为单条线,单线生产能力40万吨/年;氨肟化装置为单条线,单线生产能力30万吨/年等。 据了解,装置顺利投产后产品将能满足以高速纺切片为主的己内酰胺高端市场对产品质量的要求,不仅带来可观的经济收益,还可以实现由传统煤化工企业向高端化工、新材料领域的转变。对于促进企业和区域经济社会高质量发展意义重大。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。