牌号简介 About |
---|
较轻的树脂是由PTA和MEG生产的聚对苯二甲酸乙二醇酯。这些是专门为生产饮料、食品和其他热成型液体容器而设计的。有几种较轻的PET聚合物,设计用于不同应用的特定性能要求,包括非常好的机械性能,极好的清晰度,以及在所有注塑机和拉伸吹塑机上广泛的加工范围。较轻的C88特别适用于矿泉水的装瓶,因为它是专门为减少乙醛的形成而设计的。一般来说,对于蒸馏水和碳酸矿泉水,建议使用该等级。更轻的C88也适用于生产挤压热成型板。 Lighter Resins are polyethylene terephthalate produced from PTA and MEG. These are specifically designed for the production of beverage, food and other liquid containers for thermoforming. There are several LIGHTER PET polymers, designed for the specific performance requirements of different applications, including very good mechanical properties, excellent clarity, and a wide processing range on all injection and stretch blow molding machines. LIGHTER C88 is particularly suitable for bottling mineral water since it is designed specifically to minimize the formation of acetaldehyde. In general this grade is recommended for bottles for both still and carbonated mineral water. LIGHTER C88 is also suitable for the production of extruded thermoformable sheets. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表观密度 Apparent density |
0.88 | g/cm³ | 内部方法 |
粘度值 Viscosity value |
|||
降低的粘度 Reduced viscosity |
88.0 | ml/g | 内部方法 |
含水率 Moisture content |
< 4000 | ppm | 内部方法 |
Acetaldehyde Acetaldehyde |
< 1.0 | ppm | 内部方法 |
结晶度 Crystallinity |
> 50 | % | 内部方法 |
Weight(100 Granules) Weight(100 Granules) |
g | 内部方法 | |
固有粘度 Intrinsic viscosity |
dl/g | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
屈服 yield |
MPa | ISO 527-2 | |
断裂 fracture |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
ISO 527-2 | ||
屈服 yield |
% | ISO 527-2 | |
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | 内部方法 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
彩色坐标 Color coordinates |
|||
b b |
内部方法 | ||
颗粒大小分布 Particle size distribution |
ppm | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
霍尼韦尔UOP助力国际环保大趋向
2018-05-31 5月22日,霍尼韦尔(中国)有限公司环境保护研究院在京正式揭牌成立。在仪式上,霍尼韦尔发布了首份产业绿色升级报告。在报告中,霍尼韦尔就各类大气环境问题给出了相应的解决方案,包括用于生产高辛烷值汽油的连续催化重整技术(CCR)、降低工业排放的低氮燃烧技术,以及低挥发性有机物(VOCs)排放的涂料配方等。 同天,霍尼韦尔UOP中国区总经理刘茂树和霍尼韦尔UOP研发总监韦丹华接受采访,具体而细致地向各位来宾介绍霍尼韦尔UOP的独到之处。 历史悠久却 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |