| 牌号简介 About |
|---|
| Premi-Glas® 1286是一种玻璃纤维增强的热固性片材成型化合物，采用混合乙烯基酯/聚酯树脂技术，用于汽车动力总成和其他结构或半结构应用。主要特点和优点：优良的热性能和高温保持率。取代铸造金属以降低噪音、振动和粗糙度。对汽车化学品和盐雾有极好的抵抗力。符合GMP.UP.018和其他规范的要求。设计用于大跨度阀盖的压缩成型。 Premi-Glas® 1286 is a fiberglass reinforced thermoset sheet molding compound employing hybrid vinyl ester/polyester resin technology for automotive powertrain and other structural or semi-structural applications. Key Features and Benefits: Excellent thermal properties and elevated temperature modulus retention. Replaces cast metals for reduced Noise, Vibration, and Harshness. Excellent resistance to automotive chemicals and salt spray. Meets the requirements of GMP.UP.018 and other specs. Designed for compression molding of large-span valve covers. |
产品描述 Product Description
用途：片材;构件;汽车的发动机罩下的零件;
加工条件：压缩模塑
性能特点： 机械强度好; 抗盐水/雾; 耐化学性; 减震; Good Rigidity,noise reduction,Solvent resistance,Resistance to salt water/fog
填料：玻璃纤维
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.81 | g/cm³ | |
|
收缩率 Shrinkage rate |
0.010 | % | |
|
吸水率 Water absorption rate |
|||
|
23℃，24hr 23℃，24hr |
0.10 | % | ISO 62 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
ISO 527-2 | ||
|
23℃，模压成型 23 ℃, molded |
14000 | MPa | ISO 527-2 |
|
150℃，模压成型 150 ℃, molded |
9300 | MPa | ISO 527-2 |
|
拉伸强度 tensile strength |
ISO 527-2 | ||
|
屈服，23℃，模压成型 Yield, 23 ℃, molded |
MPa | ISO 527-2 | |
|
屈服，150℃，模压成型 Yield, 150 ℃, molded |
MPa | ISO 527-2 | |
|
弯曲模量 Bending modulus |
ISO 178 | ||
|
23℃，模压成型 23 ℃, molded |
MPa | ISO 178 | |
|
150℃，模压成型 150 ℃, molded |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
ISO 178 | ||
|
23℃，模压成型 23 ℃, molded |
MPa | ISO 178 | |
|
150℃，模压成型 150 ℃, molded |
MPa | ISO 178 | |
|
泊松比 Poisson's ratio |
|||
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
模压成型 Compression Molding |
J/m | ASTM D4812 | |
|
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
ISO 6603-2 | ||
|
模压成型，Total Penetration Energy Total Penetration Energy |
J | ISO 6603-2 | |
|
模压成型，Energy to Peak Force Compression molding, Energy to Peak Force |
J | ISO 6603-2 | |
|
High Speed Impact High Speed Impact |
ISO 6603-2 | ||
|
Deflection at Peak Load Deflection at Peak Load |
mm | ISO 6603-2 | |
|
Impact at Peak Load Impact at Peak Load |
N | ISO 6603-2 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
玻璃化转变温度 Glass transition temperature |
℃ | ISO 6721 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD TD |
1/℃ | ||
|
MD MD |
1/℃ | ||
|
导热系数 Thermal conductivity coefficient |
W/m/K | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
万华全球研发中心竣工投产，开发化工领域新产品、新技术和新材料
2021-07-16 搜料网资讯： 据近日媒体报道，万华化学集团股份有限公司全球研发中心及总部基地（一期）建设项目于日前已竣工投产。该研发中心功能为开发化工领域新产品、新技术和新材料，进 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付