| 牌号简介 About |
|---|
| Amodel® A-6135 HN聚邻苯二甲酰胺（ppa）是一种35%的玻璃纤维增强树脂，具有热稳定、润滑和热水可塑性。该树脂的关键性能是在较宽的温度范围内具有较高的耐热性、高强度和刚度。它还具有低吸湿性、优异的耐化学性和优良的电气性能。Amodel® A-6135 HN树脂是理想的汽车电气和电子应用，包括连接器，插座，开关和传感器。它也是保护关键控制系统（如防抱死制动器、牵引力控制、转向、电子发动机控制、变速箱和底盘控制单元）的发动机罩下外壳的理想选择。黑色：A-6135 HN BK 324 Natural A-6135 HS NT Amodel® A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, non-lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength and stiffness over a broad temperature range. It also exhibits low moisture absorption, excellent chemical resistance and excellent electrical properties. Amodel® A-6135 HN resin is ideal for automotive electrical and electronic applications, including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units. Black: A-6135 HN BK 324 |
产品描述 Product Description
用途：电器外壳;电气/电子应用领域;机器/机械部件;连接器;动力/其它工具;金属取代;外壳;阀门/阀门部件;草坪和园林设备;汽车领域的应用;工业应用;通用;工业部件;汽车电子;汽车的发动机罩下的零件;
颜色：黑色
加工条件：水温模具注塑成型
性能特点： 低吸湿性; 热稳定性好; 机械强度好; 耐化学性; 耐高温; 易流动; 韧性好; Good Rigidity,Good flexibility,Good liquidity,High Heat Resistance,Solvent resistance,Low moisture absorption,Heat Stabilized
填料：玻璃纤维 35
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.45 | g/cm³ | ISO 1183/A |
|
收缩率 Shrinkage rate |
ISO 294-4 | ||
|
TD TD |
0.90 | % | ASTM D955 |
|
MD MD |
0.60 | % | ASTM D955 |
|
TD TD |
1.0 | % | ISO 294-4 |
|
MD MD |
0.50 | % | ISO 294-4 |
|
吸水率 Water absorption rate |
|||
|
24hr 24hr |
% | ASTM D570 | |
|
23℃，24hr 23℃，24hr |
% | ISO 62 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
|
23℃ 23℃ |
kJ/m² | ISO 180 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，退火，3.2 mm 1.8 MPa, annealed, 3.2 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
|
熔融温度 Melting temperature |
℃ | ASTM D570 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD TD |
ASTM E831 | ||
|
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
|
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
|
MD MD |
ASTM E831 | ||
|
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
|
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
ISO 527-2 | ||
|
23℃ 23℃ |
MPa | ISO 527-2 | |
|
100℃ 100℃ |
MPa | ISO 527-2 | |
|
150℃ 150℃ |
MPa | ISO 527-2 | |
|
175℃ 175℃ |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
ISO 527-2 | ||
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
|
断裂，24℃ Fracture, 24 ℃ |
MPa | ISO 527-2 | |
|
断裂，150℃ Fracture, 150 ℃ |
MPa | ISO 527-2 | |
|
断裂，175℃ Fracture, 175 ℃ |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
ISO 527-2 | ||
|
断裂 fracture |
% | ASTM D638 | |
|
断裂，23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
|
断裂，24℃ Fracture, 24 ℃ |
% | ISO 527-2 | |
|
断裂，150℃ Fracture, 150 ℃ |
% | ISO 527-2 | |
|
断裂，175℃ Fracture, 175 ℃ |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲模量 Bending modulus |
ISO 178 | ||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
100℃ 100℃ |
MPa | ISO 178 | |
|
150℃ 150℃ |
MPa | ISO 178 | |
|
175℃ 175℃ |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
ISO 178 | ||
|
3.50% 应变，23℃ 3.50% strain, 23 ℃ |
MPa | ISO 178 | |
|
3.50% 应变，100℃ 3.50% strain, 100 ℃ |
MPa | ISO 178 | |
|
3.50% 应变，150℃ 3.50% strain, 150 ℃ |
MPa | ISO 178 | |
|
3.50% 应变，175℃ 3.50% strain, 175 ℃ |
MPa | ISO 178 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
剪切强度 shear strength |
MPa | ASTM D732 | |
|
泊松比 Poisson's ratio |
ASTM E132 | ||
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
美国再挥制裁大棒，伊朗粮农产业受影响
2020-10-18 搜料网资讯： 自2018年5月美国单方面退出伊核协议以来，美国对伊朗实施了史上最严制裁，制裁涵盖伊朗金融、交通运输、能源等方方面面。而就在本月8日，美国再次宣布对伊朗的18家 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付