| 牌号简介 About |
|---|
| RIALOX® B 120 GF30 ST F V-0 natural是一种基于聚对苯二甲酸丁二醇酯（PBT）的半结晶热塑性阻燃建筑材料，用30%的玻璃纤维增强。RIALOX® B 120 GF30 ST F V-0 natural将通过注射成型进行加工。适用于需要无卤PBT及消防设备的部位。该产品有各种颜色可供选择。RIALOX® B 120 GF30 ST F V-0 natural具有以下特性：UL 94 V-0从0.4 mm跟踪电阻600 V GWIT 775°C在3 mm GWFI 960°C从0.75 mm符合非常好的尺寸稳定性非常好的延伸性能WEEE和RoHS符合性 RIALOX B 120 GF30 ST F V-0 natural is a semi-crystalline thermoplastic flame-retardant construction material based on polybutylene terephthalate (PBT), reinforced with 30% glass fibers. RIALOX B 120 GF30 ST F V-0 natural will be processed by injection molding. It is used for parts for which a halogen-free PBT with fire protection equipment is required. The product is available in all colours. RIALOX B 120 GF30 ST F V-0 natural is characterized by the following properties: UL 94 V-0 from 0.4 mm Tracking resistance 600 V GWIT 775 °C conform at 3 mm GWFI 960 °C from 0.75 mm Very good dimensional stability Very good elongation behavior WEEE and RoHS conformity |
产品描述 Product Description
颜色：自然色,可用颜色
加工条件：注射成型 Injection Molding
性能特点： 无卤; 半结晶; 防火阻燃等级V-0; 尺寸稳定性好; 阻燃; Good Dimensional Stability,Halogen free,Flame Characteristics,Hypocrystalline,V-0
填料：玻璃纤维 30
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.51 | g/cm³ | ISO 1183 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
250℃，2.16 kg 250℃，2.16 kg |
3.50 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
ISO 294-4 | ||
|
TD TD |
0.20 到 0.60 | % | ISO 294-4 |
|
MD MD |
0.10 到 0.40 | % | ISO 294-4 |
|
吸水率 Water absorption rate |
ISO 62 | ||
|
饱和，23℃ Saturation, 23 ℃ |
0.40 | % | ISO 62 |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ISO 527-2/5 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2/5 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
B50 B50 |
℃ | ISO 306 | |
|
最高工作温度 Maximum operating temperature |
|||
|
Continuous Continuous |
℃ | ||
|
Short Time Short Time |
℃ | ||
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电常数 Dielectric constant |
IEC 60250 | ||
|
100 Hz 100 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
4.00 mm 4.00 mm |
UL 94 | ||
|
灼热丝可燃性指数 Glowing wire flammability index |
|||
|
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
|
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
|
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
西方树脂19周年厂庆 “新终点，新飞跃”
2015-12-23 秋收冬藏，金猴报喜，在这承前启后，即将开启新一年的日子里，东方树脂迎来了建厂19周年，也迎来了具有里程碑意义的一年。12月18日晚，公司高层领导及全体员工、全国各地经销商代表、杏坛镇领导嘉宾等社会各界人士共聚一起，满怀喜悦共同庆祝东方树脂成立19周年。 总经理吴少明先生发表了题为“新起点，新飞跃”的精彩开幕致辞。在致辞报告中，吴总首先回顾了过去，指出15年是艰难的一年，整个胶粘剂市场非常不景气，但东方树脂依旧在稳步向前!公司不仅被中国农业银行评为“黄金客户”，参与起草的《鞋 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付