牌号简介 About |
---|
HCG2520MP是一种高刚性、平衡韧性20%的GFPC树脂。它具有优良的表面性能、较高的NCVM率、易加工性、高稳定性和超强的形状阻力。HCG2520MP主要用于手机 HCG2520MP is high rigidity and balance tenacity 20%GF PC resin. It has excellent surface, high NCVM rate, easy to machining, high stability and super shape resistance property. HCG2520MP is mainly used in mobile phone |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.34 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
18 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.10 到 0.30 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
100 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
2.0 | % | ASTM D638 |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
美瑞新材上半年完成净利超2000万 同比增长66%
2017-08-11 美瑞新材披露2017年半年报,公司上半年实现营业收入2.36亿元,同比增长71.06%;净利润为2196.41万元,同比增长65.73%。 美瑞新材表示公司持续加大新产品研发和市场推广力度,加强质量管理,产品质量稳定性和设备稳定性持续提高,生产效率持续提高。在巩固原有市场的基础上,不断进行横向行业拓展和新产品市场开拓, 经营业绩快速增长。 值得注意的是,美瑞新材于今年3月9日向证监会调了首次公开发行股票并在创业板上市的申请,3月30日公司申请 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |