牌号简介 About |
---|
Clearflex® FF D0是一种线性低密度聚乙烯,含抗氧化剂,适用于吹膜技术。该产品具有非常低的密度和高分子量。Clearflex® FF D0制成的薄膜具有高度的透明性,具有优异的密封性能,主要是在低温下,具有优异的机械性能。主要用途Clearflex® FF D0被推荐用于生产拉伸薄膜,由于其独特的性能被用于混合或共挤。 Clearflex FF D0 is a linear low density polyethylene, with antioxidants, suitable for blown film technology. The product is characterised by a very low density and high molecular weight. Films made with Clearflex FF D0 are highly transparent, have excellent sealing properties, mainly at low temperature, and outstanding mechanical performances. Main Application Clearflex FF D0 is recommended to produce stretch film and is used in blend or coextrusion because of its unique properties. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.80 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
与自身 - 动态,吹塑薄膜 Self dynamic, blow molded film |
> 0.50 | ISO 8295 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
10 to 50µm | ||
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,吹塑薄膜 1% secant, MD, blow molded film |
65.0 | MPa | ISO 527-3 |
1% 正割,TD,吹塑薄膜 1% secant, TD, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,吹塑薄膜 MD, yield, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,吹塑薄膜 TD, yield, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,吹塑薄膜 MD, fracture, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,吹塑薄膜 TD, fracture, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,吹塑薄膜 MD, fracture, blow molded film |
% | ISO 527-3 | |
TD,断裂,吹塑薄膜 TD, fracture, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact 2 |
|||
吹塑薄膜 Blown film 2 |
g | ISO 7765-1/A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 3 |
ISO 6383-2 | ||
MD MD |
kN/m | ISO 6383-2 | |
TD TD |
kN/m | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,吹塑薄膜 45 °, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
吹塑薄膜 Blown film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
3 Blown Film |
【新闻资讯】查看全部
中原石化使用HA-R催化剂生产电容器膜料
2021-06-29 搜料网资讯: 6月25日,中原石化使用HA-R催化剂成功生产出更高质量的电容器膜料,标志着电容器膜料走向高端化,加快电容器膜料替代进口,实现国产化。 HA-R催化剂具有高聚合活性、 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |