FLEXAREN® 14010-优质乙烯-醋酸乙烯酯共聚物,含14%的醋酸乙烯酯。采用高压管状工艺制造。FLEXAREN® 14010比LDPE更具弹性,可与多种聚合物相容。它可以用相同的设备进行加工。 FLEXAREN® 14010 - high quality ethylene vinyl acetate copolymer with 14% content of vinyl acetate. Manufactured by high pressure tubular process. FLEXAREN® 14010 is more elastic than LDPE and compatible with a wide range of polymers. It can be processed with the same equipment. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
20℃ 20℃ |
0.934 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
10 | g/10min | ISO 1133 |
醋酸乙烯含量 Vinyl acetate content |
14.0 | wt% | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
60.0 | ℃ | ISO 306/A |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A Shaw's A |
90 | ISO 868 | |
邵氏 D Shaw's D |
ISO 868 | ||
拉伸强度 tensile strength |
ISO 527-2/1BA | ||
断裂 fracture |
MPa | ISO 527-2/1BA | |
50% 应变 50% strain |
MPa | ISO 527-2/1BA | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/1BA |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
日本氟制造商将PTFE导管内衬产量翻倍,应对市场短缺问题
2022-01-27 聚四氟乙烯(PTFE)用于导管以减少摩擦,而氟化乙烯丙烯 (FEP) 热缩管提供柔韧性、透明度和润滑性。在所有情况下,这些材料都能提高患者的舒适度和护理效率。 日本氟聚合物制造商J |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |