牌号简介 About |
---|
高性能热塑性材料、无增强聚醚醚酮(PEEK)、半结晶、特殊挤压工艺用深度过滤颗粒、标准流程、符合FDA食品接触标准、颜色自然/米色。金属丝包衣、长丝挤压、细管、薄膜。耐腐蚀环境的化学性,适用于医疗和食品接触应用的灭菌。 High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, depth filtered granules for specialty extrusion processes, standard flow, FDA food contact compliant, colour natural/beige. Wire coating, extrusion of filaments, minitubes, films. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications. |
产品描述 Product Description
厂家:英国威格斯 Victrex
类别:PEEK
用途:医疗/护理用品;薄膜;非特定食品应用;细丝;涂层应用;管件;
颜色:自然色,米黄色
加工条件:涂层,薄膜挤出,细丝挤出 Film extrusion,Extrusion
性能特点: 半结晶; 耐化学性; 易消毒; 食品接触; 易流动; Good liquidity,Hypocrystalline,Good disinfection,Solvent resistance,Food contact compliance
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,23℃ Shore D, 23 ℃ |
85 | ISO 868 | |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
4000 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
98.0 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
45 | % | ISO 527-2 |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
3800 | MPa | ISO 178 |
弯曲强度 bending strength |
ISO 178 | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ISO 178 | |
125℃ 125℃ |
MPa | ISO 178 | |
175℃ 175℃ |
MPa | ISO 178 | |
275℃ 275℃ |
MPa | ISO 178 | |
压缩强度 compressive strength |
ISO 604 | ||
23℃ 23℃ |
MPa | ISO 604 | |
120℃ 120℃ |
MPa | ISO 604 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
ISO 179 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
ISO 180 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
玻璃化转变温度 Glass transition temperature |
ISO 11357-2 | ||
-- -- |
℃ | ISO 11357-2 | |
-- -- |
℃ | ISO 11357-2 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
ISO 11359-2 | ||
< 143℃ < 143℃ |
cm/cm/℃ | ISO 11359-2 | |
> 143℃ > 143℃ |
cm/cm/℃ | ISO 11359-2 | |
MD MD |
ISO 11359-2 | ||
< 143℃ < 143℃ |
cm/cm/℃ | ISO 11359-2 | |
> 143℃ > 143℃ |
cm/cm/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
ISO 22007-4 | ||
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
IEC 60093 | ||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
125 ℃ 125 ℃ |
ohms·cm | IEC 60093 | |
275 ℃ 275 ℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
IEC 60243-1 | ||
0.05 mm 0.05 mm |
kV/mm | IEC 60243-1 | |
2 mm 2 mm |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
IEC 60250 | ||
23 ℃,50 Hz 23 ℃,50 Hz |
IEC 60250 | ||
200 ℃,50 Hz 200 ℃,50 Hz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glowing wire flammability index |
|||
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Extreme oxygen index |
ISO 4589-2 | ||
-- -- |
% | ISO 4589-2 | |
-- -- |
% | ISO 4589-2 | |
毒性 toxicity |
NES 713 | ||
CO content CO content |
NES 713 | ||
CO2 content CO2 content |
NES 713 | ||
Total gases Total gases |
NES 713 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
螺旋流动长度 Spiral flow length |
cm | Internal Method | |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
% | ISO 294-4 | |
MD MD |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
饱和,100℃ Saturation, 100 ℃ |
% | ISO 62 | |
熔体表观粘度 Apparent viscosity of melt |
|||
400℃ 400℃ |
Pa·s | ISO 11443 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Crystalline |
3 模具温度: 338°F, 熔体温度: 698°F |
4 1 mm |
5 370°C nozzle |
6 Onset |
7 Midpoint |
8 Average |
9 Along flow |
10 0.4 mm |
11 3.2 mm |
【新闻资讯】查看全部
兰州石化茂金属聚烯烃工业试生产成功!创国内新纪录!
2021-06-07 我在想: 5月28日11时, 石化厂聚丙烯装置成功生产出 茂金属聚丙烯纤维料产品, 标志着公司茂金属聚丙烯纤维料首次工业试生产成功, 创造国内同类产品开车一次成功历史纪录 是该产 |
兰州石化茂金属聚烯烃工业试生产成功!创国内新纪录! 我在想:5月28日11时,石化厂聚丙烯装置成功生产出茂金属聚丙烯纤维料产品,标志着公司茂金属聚丙烯纤维料首次工业试生产成功,创造国内同类产品开车一次成功历史纪录是该产品向规模化生产迈出的关键一步,为国内同类产品生产积累了宝贵经验。
石化院兰州中心2018年完成“茂金属聚丙烯纤维料的中试开发”研究项目,依托该项目形成的中试技术,在集团公司聚烯烃重大科技专项立项研究,这不仅是聚丙烯装置贯彻公司新发展理念、打造高端特色产品的攻坚项目,也是实现提质增效、提升核心竞争力的关键突破点。 为确保试生产一次成功,公司多次组织对方案讨论研究,根据聚丙烯装置硬件设备条件,反复逐项核对工艺控制难点要点,突破装置原工艺设计,最终制定出茂金属聚丙烯纤维试生产方案,并在试生产前对各项方案要求进行逐条落实准备。 5月27日上午9时8分,装置正式投入茂金属催化剂建立反应,各级管理技术人员及岗位员工全力投入试生产中,连续60多个小时盯守装置,根据生产情况不断调整工艺指标,对试生产过程中突发问题深入讨论、及时解决,进一步摸索装置最佳生产控制条件。 5月28日11时,装置成功生产出合格产品,5月29日17时,产品试生产阶段顺利完成,创造了国内茂金属聚丙烯纤维料开车一次成功的历史纪录,获得了宝贵的经验,为聚丙烯装置产品序列再添新丁,为公司高质量发展再立新功。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。