牌号简介 About |
---|
Westlake聚乙烯EF311是一种低密度聚乙烯,建议用于铸膜澄清应用。这种材料具有很好的光学性能,建议用于面包薄膜和软制品包装。应用/使用面包袋软商品包装高清晰度包装 WESTLAKE polyethylene EF311 is a low-density polyethylene suggested for cast film clarity applications. This material has very good optical properties, and is suggested for bakery films and soft goods packaging. Application/Uses Bakery bags Soft goods packaging High clarity packaging |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.923 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.2 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:32 µm,吹塑薄膜 1% secant, MD: 32 µ m, blow molded film |
165 | MPa | ASTM D882 |
1% 正割,TD:32 µm,吹塑薄膜 1% secant, TD: 32 µ m, blow molded film |
193 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,32 µm,吹塑薄膜 MD, fracture, 32 µ m, blow molded film |
22.8 | MPa | ASTM D882 |
TD,断裂,32 µm,吹塑薄膜 TD, fracture, 32 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,32 µm,吹塑薄膜 MD, fracture, 32 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,32 µm,吹塑薄膜 TD, fracture, 32 µ m, blow molded film |
% | ASTM D882 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,31.8 µm,吹塑薄膜 45 °, 31.8 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
31.8 µm,吹塑薄膜 31.8 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
落锤冲击 Drop hammer impact 2 |
|||
31.8 µm 31.8 µm 2 |
kN/m | ASTM D1709 |
备注 |
---|
2 Blown Film |
【新闻资讯】查看全部
化销华南首次打通 乙烯产品公路运输流程
2022-01-25 1月16日,中科炼化首车低温乙烯顺利装车出厂,这标志着中科炼化成为华南区域首家掌握运用低温乙烯装车技术的化工生产企业。 为保证乙烯裂解装置高负荷运行,中科炼化在EVA装置尚 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |