| 牌号简介 About |
|---|
| Bayflex 110-35 IMR系统生产的固体聚氨酯弹性体在室温下的弯曲模量约为33500 psi*。该系统用于提供多种大型反应注射成型（RIM）零件，如汽车蒙皮。该系统包含内部模具释放（IMR），与磨制玻璃纤维或矿物增强材料一起使用。Bayflex 110-35 IMR是作为两种液体成分提供的配方RIM系统。A组分为二苯基甲烷二异氰酸酯（MDI）预聚物，B组分为聚醚多元醇体系。与任何产品一样，在给定应用中使用Bayflex 110-35 IMR系统必须由用户提前进行测试（包括现场测试等），以确定适用性。 Bayflex 110-35 IMR system produces a solid urethane elastomer which has a flexural modulus of approximately 33,500 psi* at room temperature. This system is used to provide multiple releases of large reaction injection molding (RIM) parts, such as automotive fascias. The system contains internal mold release (IMR) and is used with milled glass fiber or mineral reinforcements. Bayflex 110-35 IMR is a formulated RIM system supplied as two liquid components. Component A is a diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol system. As with any product, use of the Bayflex 110-35 IMR system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
产品描述 Product Description
用途：饰带;汽车领域的应用;
加工条件：反应注射成型 (RIM)
填料：玻璃纤维/矿物
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.13 | g/cm³ | ASTM D792 , ASTM D1622 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.2 mm MD：3.2 mm |
0.56 | % | 内部方法 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
断裂，3.18 mm Fracture, 3.18 mm |
15.2 | MPa | ASTM D412 |
|
断裂，3.18 mm Fracture, 3.18 mm |
15.2 | MPa | ASTM D638 |
|
拉伸应变 Tensile strain |
|||
|
断裂，3.18 mm Fracture, 3.18 mm |
110 | % | ASTM D412 |
|
断裂，3.18 mm Fracture, 3.18 mm |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
ASTM D790 | ||
|
-30℃，3.18 mm -30℃，3.18 mm |
MPa | ASTM D790 | |
|
23℃，3.18 mm 23℃，3.18 mm |
MPa | ASTM D790 | |
|
65℃，3.18 mm 65℃，3.18 mm |
MPa | ASTM D790 | |
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
撕裂强度 tear strength 2 |
|||
|
3.18 mm 3.18 mm 2 |
kN/m | ASTM D624 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
3.2mm 3.2mm |
J/m | ASTM D256 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Heat Sag（6 in Overhang，121℃，3.18 mm） Heat Sag（6 in Overhang，121℃，3.18 mm） 4 |
mm | ASTM D3769 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：3.2 mm MD：3.2 mm |
1/℃ | ASTM D696 | |
|
热固组件 Thermosetting components 3 |
|||
|
部件 A Component A |
|||
|
部件 B Component B |
|||
|
脱模时间 stripping time |
min | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 C 模具 |
| 3 105 Index |
| 4 1 hr |
|
【新闻资讯】查看全部 
2021年全国吸收外资超1.1万亿元， 同比增长14.9%
2022-01-14 搜料网资讯： 商务部1月13日发布数据显示，2021年，全国实际使用外资金额11493.6亿元人民币，同比增长14.9%(折合1734.8亿美元，同比增长20.2%)。 从行业看，服务业实际使用外资金额9064.9亿 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付