| 牌号简介 About |
|---|
| KetaSpire KT- 880 CF30是高流动性 、30 ％碳纤增强聚醚醚酮（ PEEK）。 在温度接近300℃时，碳纤增强 KetaSpire PEEK 的机械性能达到行业最高水平，并且，具有KetaSpire 产品系列最低的线性热膨胀系数。KetaSpire PEEK按照最高的行业标准加工，以兼具各种出色的性能为特征，包括优异的耐磨损性、一流的抗疲劳性、易于熔融加工、高纯度、优异的耐有机物、酸和碱等化学物质的性能。 这些特性使得它非常适合医疗保健、交通运输、电子、化学处理和其它工业用途。 KetaSpire® KT-880 CF30 is a high flow, 30% carbon fiber reinforced grade of polyetheretherketone (PEEK). Carbon-fiber reinforcement of KetaSpire® PEEK provides the maximum levels of mechanical properties at temperatures approaching 300°C and the lowest coefficient of linear thermal expansion within the KetaSpire® product family. KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity and excellent chemical resistance to organics, acids and bases. These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing and other industrial uses. |
产品描述 Product Description
用途：医疗/护理用品;薄膜;医疗器械;电气/电子应用领域;连接器;外科器械;飞机应用;石油/天然气用品;牙齿应用领域;泵件;工业应用;密封件;医疗器材;
颜色：黑色
加工条件：型材挤出成型 Profile extrusion
性能特点： 防火阻燃等级V-0; 蒸汽消毒; 耐化学性; 放射线可穿透; 辐射消毒; 阻燃; 流动性高; 加热消毒; 机械强度好; 尺寸稳定性好; 高压灭菌器消毒; 耐疲劳性好; 抗伽马射线; 易消毒; 耐高温; 耐蒸汽; 环氧乙烷消毒; 电子束消毒; Good Rigidity,Good Dimensional Stability,High liquidity,Good disinfection,Steam sterilized,Gamma radiation,E-beam disinfection,Flame Characteristics,High pressure disinfection,High Heat Resistance,Radioactive,Fatigue resistance,Radiation disinfection,Solvent resistance,Resistance to the steam,Ethylene oxide disinfection,Heat sterilization,V-0
填料：碳纤维 30
| 技术参数 Technical Data | |||
|---|---|---|---|
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
-- -- |
64 | J/m | ASTM D256 |
|
-- -- |
8.5 | kJ/m² | ISO 180 |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
-- -- |
640 | J/m | ASTM D4812 |
|
-- -- |
43 | kJ/m² | ISO 180 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，退火 1.8 MPa, annealed |
315 | ℃ | ASTM D648 |
|
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
|
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：-50~50℃ MD：-50~50℃ |
1/℃ | ASTM E831 | |
|
比热 specific heat |
DSC | ||
|
50℃ 50℃ |
J/kg/℃ | DSC | |
|
200℃ 200℃ |
J/kg/℃ | DSC | |
|
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
0.80 mm 0.80 mm |
UL 94 | ||
|
1.60 mm 1.60 mm |
UL 94 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
M 级 M-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
|||
|
-- -- |
MPa | ASTM D638 | |
|
-- -- |
MPa | ISO 527-2/1A/1 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ISO 527-2/1A/5 | |
|
-- -- |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture 5 |
% | ASTM D638 | |
|
断裂 fracture |
% | ISO 527-2/1A/5 | |
|
弯曲模量 Bending modulus |
|||
|
-- -- |
MPa | ASTM D790 | |
|
-- -- |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
-- -- |
MPa | ASTM D790 | |
|
-- -- |
MPa | ISO 178 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
剪切强度 shear strength |
MPa | ASTM D732 | |
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
g/cm³ | ASTM D792 | |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
400℃，2.16kg 400℃，2.16kg |
g/10min | ASTM D1238 | |
|
收缩率 Shrinkage rate 4 |
ASTM D955 | ||
|
MD：3.2 mm MD：3.2 mm |
% | ASTM D955 | |
|
TD：3.2 mm TD：3.2 mm |
% | ASTM D955 | |
|
吸水率 Water absorption rate |
|||
|
24hr 24hr |
% | ASTM D570 | |
|
熔体表观粘度 Apparent viscosity of melt |
|||
|
400℃，1000 sec^-1 400℃，1000 sec^-1 |
Pa·s | ASTM D3835 | |
| 备注 |
|---|
| 1 Passes 60s VB flame, smoke and toxicity requirements. |
| 2 一般属性：这些不能被视为规格。 |
| 3 5" x 0.5" x 0.125" bars |
| 4 0.20 in/min |
|
【新闻资讯】查看全部 
手提塑料袋及一次性塑料杯使用量减少100%，泰国2022年限塑动真格
2022-01-14 搜料网资讯： 据泰国头条新闻编译报道，当地时间1月10日，泰国污染控制厅根据内阁发布的《2018-2030年塑料垃圾管理方案》，加快实施塑料垃圾管理，在全国政府机构开展垃圾减量分类 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |