| 牌号简介 About |
|---|
| 西湖低密度聚乙烯EC1390主要用于需要快速生产线速度和相对较低涂层重量的挤出涂层应用。与其他熔融指数较低的低密度聚乙烯涂层材料相比，EC1390对纸张基材的粘附性稍好，可以在较低的温度下进行热封。然而，高熔融指数涂层材料产生的颈部略多和较窄的热封温度。EC1390-1390P WESTLAKE low-density polyethylene EC1390 is used primarily in extrusion-coating applications that require fast line speeds and relatively low coating weights. When compared with other low-density polyethylene coating materials that have considerably lower melt indexes, EC1390 has slightly better adhesion to paper substrates and can be heat-sealed at a slightly lower temperature. However, high melt index coating materials produce slightly more neck-in and a narrower heat-sealing temperature. EC1390 - 1390P |
产品描述 Product Description
用途：涂层应用;
加工条件：涂层
性能特点： 粘结性好; Kosher certification,Good bond
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.915 | g/cm³ | ASTM D4883 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
15 | g/10min | ASTM D1238 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength 2 |
|||
|
断裂，23℃ Fracture, 23 ℃ 2 |
9.00 | MPa | ASTM D638 |
|
拉伸应变 Tensile strain 2 |
|||
|
断裂，23℃ Fracture, 23 ℃ 2 |
300 | % | ASTM D638 |
|
弯曲模量 Bending modulus 3 |
|||
|
2% 正割，23℃ 2% secant, 23 ℃ 3 |
193 | MPa | ASTM D790 |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 类型 4, 20 in/min |
| 3 0.50 in/min |
|
【新闻资讯】查看全部 
VDMA：工业4.0成2016年K展上橡塑机械展出亮点
2016-10-20 “让工业4.0成为现实”是VDMA塑料橡胶机械协会及其成员公司为K 2016年设定的目标。“K 2016的口号是‘工业 4.0 - working for you’! |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付