牌号简介 About |
---|
纤维素增强苯酚改性三聚氰胺模塑料具有很好的电气性能、优异的表面硬度、良好的机械性能、良好的紫外线稳定性和良好的耐热性。主要用途:家用电器配件。本产品符合重金属和PCA的允许上限,也符合根据ISO 14528-1:MP(LD30+MD15)、X、E-(LD40+MD05)、X、E DIN7708:MP 181.5,欧盟指令2002/95(RoHS)、2002/96(WEEE)和2006/122(PFOS)标识的要求 Cellulose reinforced phenol modified Melamine moulding compound Very good electrical properties, excellent surface hardness, good mechanical properties, good UV stability and good heat resistance Primary application(s): Mountings for household appliances This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) Identification according to ISO 14528-1: MP (LD30+MD15), X, E - (LD40+MD05), X, E DIN 7708: MP 181.5 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.60 到 1.70 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.55 到 0.75 | g/cm³ | ISO 60 |
收缩率 Shrinkage rate |
ISO 2577 | ||
MD MD 3 |
0.80 到 1.2 | % | ISO 2577 |
MD MD 4 |
0.50 到 0.90 | % | ISO 2577 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
< 2.0 | % | ISO 62 |
后收缩 Post contraction 5 |
% | ISO 2577 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
ISO 527-2 | ||
模压成型 Compression Molding |
MPa | ISO 527-2 | |
注塑成型 injection molding |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
模压成型 Compression Molding |
MPa | ISO 527-2 | |
注塑成型 injection molding |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
ISO 178 | ||
模压成型 Compression Molding |
MPa | ISO 178 | |
注塑成型 injection molding |
MPa | ISO 178 | |
弯曲强度 bending strength |
ISO 178 | ||
模压成型 Compression Molding |
MPa | ISO 178 | |
注塑成型 injection molding |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ISO 604 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
模压成型 Compression Molding |
kJ/m² | ISO 179/1eA | |
注塑成型 injection molding |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
模压成型 Compression Molding |
kJ/m² | ISO 179/1eU | |
注塑成型 injection molding |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:50~100℃ MD:50~100℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1461 | |
最高使用温度 Maximum operating temperature |
IEC 60216 | ||
<50 h <50 h |
℃ | IEC 60216 | |
20,000 h 20,000 h |
℃ | IEC 60216 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耐电弧性 Arc resistance |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
压缩成型压力 Compression molding pressure |
MPa | ||
压缩成型温度 Compression molding temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Compression Molded |
3 Injection Molded |
4 168 h / 110°C |
【新闻资讯】查看全部
万盛股份北方新材料项目成功闯关节能审查
2021-12-04 搜料网资讯: 万盛 股份重金打造的山东生产基地,取得重要进展。万盛股份旗下山东万盛新材料有限公司年产31.93万吨功能性新材料一体化生产项目,节能审查的申请已获通过,公司已 |
万盛股份北方新材料项目成功闯关节能审查 搜料网资讯:万盛股份重金打造的山东生产基地,取得重要进展。万盛股份旗下山东万盛新材料有限公司年产31.93万吨功能性新材料一体化生产项目,节能审查的申请已获通过,公司已于11月5日拿到项目的节能审查许可证。 总部位居浙江台州的万盛股份,是全球最主要的的磷系阻燃剂生产、供应商,目前拥有浙江临海杜桥医化园区、国家级泰兴经济开发区2大生产基地,临海总部、上海张江、江苏泰兴3个研发中心。目前,万盛股份已经形成了阻燃剂、胺助剂、催化剂、涂料助剂四大系列产品体系。 据悉,为了通过打通有机磷阻燃剂的上下游供应链,丰富公司目前功能性新材料产品线,万盛股份于2021年11月启动了潍坊功能性新材料项目,同意全资子山东万盛新材料有限公司在山东省潍坊滨海经济技术开发区投资建设年产55万吨功能性新材料一体化生产项目,项目总预算22.5亿元。 根据期初的投资公告,万盛股份上述新材料项目占地面积600亩,总建筑面积118800.86平方米。建成后,将形成年产55.08万吨功能性新材料的生产能力,其中三氯氧磷12万吨、五氯化磷3万吨、新材料阻燃剂及特种阻燃助剂23.21万吨、高端环氧树脂及助剂13万吨、表面活性剂3.87万吨;副产品:30%盐酸14.93万吨、氯化钠2.76万吨、硫酸钠0.08万吨、84%硫酸0.25万吨、聚氯化铝2.3万吨、氯化钙1.11万吨。项目分两期建设,预计2025年2月全部完工。 实施该项目对万盛股份意义重大,通过建立北方新材料生产基地,自主研发、生产、销售绿色功能性新材料产品,有利于完善公司产业链,掌握新材料产品技术研发和工程技术核心能力,形成以产品供应为新的经济增长点的一体化技术服务能力。 如果要用数字来概述万盛股份上述的55万吨功能性新材料项目,就是在山东潍坊再造两个万盛股份。 数据显示,2020年,万盛股份营业收入为23.3亿元,净利润为3.93亿元亿元。根据上述项目期初测算,年产55万吨功能性新材料一体化生产项目达产达效后,预计正常年营业收入73.02亿元,利润总额为12.54元。也就是说,如果万盛股份上述项目能够成功达产,根据期初预算,公司的年营业收入将迈入百亿元。这对于万盛股份来说,无异于一次飞跃。 当时,万盛股份在启动上述项目时,就在风险提示中指出,项目的实施尚需环评审批等前置审批工作,尚存在不确定性。如今,在拿到项目的节能审查许可证,也意味着上述项目的建设正在顺利推进中。 实际上,万盛股份的上述项目,也是公司的再融资募投项目。公司增发预案显示,万盛股份拟非公开发行7700万股,预计募集资金15.43亿元,募投项目即“年产31.93万吨功能性新材料一体化生产项目”。该项目计划总投资16亿元,拟使用募集资金13.5亿元。换而言之,万盛股份山东潍坊项目,与公司募投项目息息相关。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。