| 牌号简介 About |
|---|
| 阻燃聚丙烯均聚物化合物，室外应用（即体育场座椅）紫外线稳定，不含卤素，符合DIN VDE 0472第815部分的要求。 Fortron 6850L6 offers the lowest warpage available. The easy flowing nature allows this product to be injection molded into thin walled applications. The excellent balance of mineral and glass fibers result in a superior heat resistance and dimensional stability. This grade is inherently flame-retardant along with high hardness and rigidity. Especially used for thin walled by unfavorable flow length-wall thickness ratio. This is the most isotropic grade available. |
产品描述 Product Description
用途：室外应用;座椅;
加工条件：注射成型 Injection Molding
性能特点： 无卤; 防火阻燃等级V-0; 均聚物; 阻燃; 耐候抗UV; Weather resistance is good,Halogen free,Flame Characteristics,Homopolymer,V-0
紫外线：UV Stabilized
填料：玻璃纤维/矿物 50
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.80 | g/cm³ | ASTM D792 |
|
密度 Density |
1.80 | g/cm³ | ISO 1183 |
|
收缩率 Shrinkage rate |
ISO 294-4 | ||
|
TD TD |
0.30 to 0.50 | % | ASTM D955 |
|
MD MD |
0.20 to 0.40 | % | ASTM D955 |
|
TD TD |
0.40 to 0.60 | % | ISO 294-4 |
|
MD MD |
% | ISO 294-4 | |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
% | ISO 62 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
|
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
8.0 MPa，未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
|
玻璃化转变温度 Glass transition temperature 3 |
℃ | ISO 11357-2 | |
|
熔融温度 Melting temperature 5 |
℃ | ISO 11357-3 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD TD |
1/℃ | ISO 11359-2 | |
|
MD MD |
1/℃ | ISO 11359-2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
1 kHz 1 kHz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
|||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耐电弧性 Arc resistance |
sec | ASTM D495 | |
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | ASTM D3638 | |
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
0.38 mm 0.38 mm |
UL 94 | ||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Specimen Thickness（Shrinkage） Specimen Thickness（Shrinkage） |
mm | Internal Method | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A/1 | |
|
拉伸强度 tensile strength |
|||
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
|
断裂 fracture |
MPa | ISO 527-2/1A/5 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
|
断裂 fracture |
% | ISO 527-2/1A/5 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
弯曲强度 bending strength 2 |
MPa | ISO 178 | |
|
洛氏硬度 Rockwell hardness |
|||
|
M 级 M-level |
ASTM D785 | ||
|
M 级 M-level |
ISO 2039-2 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部
中天合创釜式高压聚乙烯装置一次开车成功
2017-08-09 从中国石油化工集团公司获悉，8月6日，中天合创鄂尔多斯煤炭深加工示范项目12万吨/年釜式高压聚乙烯装置，一次投料开车成功，顺利产出合格产品。标志着中天合创项目建设完美收官。 中天合创12万吨/年釜式高压聚乙烯装置自2014年11月份开工以来，累计安装完成地下管道3939米、钢结构1654吨、静设备246台、动设备163台、工艺管道97857�季丁⒎笊璧缙�仪表电缆152000米等施工任务。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付