牌号简介 About |
---|
UBE超聚乙烯Umerit是以茂金属为催化剂,气相法合成的乙烯-α-烯烃共聚物。茂金属催化方法可以获得任何靶向分子结构,从而获得优良的物理性能。因此,Umerit500F具有各种优异的性能:优越的低温密封性能,与1500F相比更具优势-在加工时降低电机负荷-高速拉伸时几乎不会发生拉伸共振。 UBE super polyethylene UMERIT® are ethylene alpha-olefin copolymers produced using metallocene catalyst by gas phase process. The metallocene catalytic method results in superior physical properties by being able to acquire any targeted molecular structures. Therefore UMERIT®500F offer various excellent properties: -Superior low temperature seal property, advantageous compared to 1500F -Reduced motor load at processing -Draw resonance at high-speed drawing hardly occurs |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.904 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
4.0 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR |
|||
F50 F50 |
1000 | hr | ASTM D1693 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temperature |
81.0 | ℃ | ASTM D1525 |
熔融温度 Melting temperature |
87.0 | ℃ | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Flexural Modulus |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
巴斯夫携手BillerudKorsnäs为软包装开发独特的家庭可堆肥层压纸
2020-12-14 搜料网资讯: ●由 BillerudKorsns 的 ConFlex Silk 纸张和巴斯夫生物聚合物ecovio 通过复膜胶 Epotal Eco 粘合而成的层压纸; ●家庭可堆肥解决方案为软包装使用后的报废处理提供更多选择; ● |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |