牌号简介 About |
---|
Valox Enh4560树脂VALOX™ ENH4560 resin是基于Valox PBT树脂的无溴/无氯阻燃产品。 VALOX ENH4560 resin is a non-brominated/non-chlorinated flame retardant product based on VALOX PBT resin. |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/2C | ||
-30℃ -30℃ |
10 | kJ/m² | |
23℃ 23℃ |
10 | kJ/m² | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/2U | ||
-30℃ -30℃ |
35 | kJ/m² | |
23℃ 23℃ |
40 | kJ/m² | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
75 | J/m | ASTM D256 |
0℃ 0℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 12 |
kJ/m² | ISO 180-1A | |
0℃ 0℃ 13 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 14 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-30℃ -30℃ |
J/m | ASTM D4812 | |
23℃ 23℃ |
J/m | ASTM D4812 | |
-30℃ -30℃ 15 |
kJ/m² | ISO 180/1U | |
23℃ 23℃ 16 |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 17 |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 18 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 19 | |
-- -- |
℃ | ASTM D1525 20 | |
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
ISO 11359-2 | ||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ||
MD:23~150℃ MD:23~150℃ |
1/℃ | ||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ||
TD:23~150℃ TD:23~150℃ |
1/℃ | ||
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257,IEC 60093 | |
介电强度 Dielectric strength |
|||
0.8 mm,在油中 0.8 mm in oil |
kV/mm | ASTM D149 | |
1.6 mm,在油中 1.6 mm in oil |
kV/mm | ASTM D149 | |
3.2 mm,在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
0.8 mm,在油中 0.8 mm in oil |
kV/mm | IEC 60243-1 | |
1.6 mm,在油中 1.6 mm in oil |
kV/mm | IEC 60243-1 | |
3.2 mm,在油中 3.2 mm in oil |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150,IEC 60250 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150,IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.80 mm 0.80 mm |
|||
3.00 mm 3.00 mm |
|||
灼热丝可燃性指数 Glowing wire flammability index |
|||
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
1 mm 1 mm |
℃ | ||
2 mm 2 mm |
℃ | ||
3 mm 3 mm |
℃ | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
填充物 Filler |
% | ASTM D229 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ISO 2039-2 | ||
球压硬度 Ball hardness |
|||
H358/30 H358/30 |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus |
|||
-- -- 1 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 2 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/5 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
屈服 yield 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/5 | |
断裂 fracture 5 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 6 |
MPa | ASTM D790 | |
-- -- 7 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 8 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 9 |
MPa | ASTM D790 | |
断裂,50 mm跨度 Fracture, 50 mm span 10 |
MPa | ASTM D790 | |
断裂弯曲应变 Fracture bending strain 11 |
% | ISO 178 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792, ISO 1183 | |
熔体质量流动速率 Melt Flow Rate |
|||
265℃,5.0kg 265℃,5.0kg |
g/10min | ASTM D1238 | |
熔体体积流动速率 Melt Volume Rate |
|||
250℃,5 kg 250℃,5 kg |
cm³/10min | ISO 1133 | |
熔体表观粘度 Apparent viscosity of melt |
|||
260℃,1500 sec^-1 260℃,1500 sec^-1 |
Pa·s | ISO 11443 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 类型 1, 0.20 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 2 mm/min |
8 80*10*4 |
9 80*10*4 mm |
10 标准 B (120°C/h), 载荷2 (50N) |
11 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
能源危机卷土重来!欧洲天然气价格飙升逾10%,创纪录新高
2021-12-22 搜料网资讯: 受俄罗斯天然气断供影响,欧洲天然气价格跃升至纪录高位。这进一步加剧欧洲电力危机,欧洲电价再创历史新高。 彭博报道称,管网运营商Gascade表示,俄罗斯天然气供 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |