牌号简介 About |
---|
LLDPE薄膜产品应用LL6208AF已开发用于重型袋、衬里和其他需要优良机械性能的薄膜应用中的丰富混合物。该等级也被推荐用于人造草地应用,其优点和特点是LL6208AF是一种线性低密度聚乙烯共聚物,以己烯-1为共聚单体。它具有以下特性:良好的冲击强度和抗穿刺性、高撕裂强度、良好的光学性能、良好的气泡稳定性、良好的密封性和热粘强度。如果需要电晕处理,其水平通常应在38-48mn/m范围内。 LLDPE film products Applications LL6208AF has been developed for use in rich blends in heavy duty sacks, liners and other thin film applications requiring excellent mechanical performance. This grade is also recommended for artificial grass applications Benefits and Features LL6208AF is a linear low density polyethylene copolymer containing hexene-1 as the co-monomer. It offers the following properties: Excellent impact strength and puncture resistance High tear strength Good optical properties Good bubble stability Excellent sealability and hot-tack strength If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.920 | g/cm³ | ISO 1183/D |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.90 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
38 | µm | |
拉伸模量 Tensile modulus |
ISO 1184 | ||
1% 正割,MD,38 µm,吹塑薄膜 1% secant, MD, 38 µ m, blow molded film |
180 | MPa | ISO 1184 |
1% 正割,TD,38 µm,吹塑薄膜 1% secant, TD, 38 µ m, blow molded film |
240 | MPa | ISO 1184 |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,38 µm,吹塑薄膜 MD, yield, 38 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,38 µm,吹塑薄膜 TD, yield, 38 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 1184 | ||
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
% | ISO 1184 | |
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
% | ISO 1184 | |
落锤冲击 Drop hammer impact |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
g | ASTM D1709-A | |
撕裂强度 tear strength |
|||
MD,38 µm,吹塑薄膜 MD, 38 µ m, blow molded film |
g | ASTM D1922 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
TD,38 µm,吹塑薄膜 TD, 38 µ m, blow molded film |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,38 µm,吹塑薄膜 45 °, 38 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
加拿大对华PET树脂作出双反初裁
2017-11-23 近日,加拿大边境服务署发布公告,对原产于或进口自中国、印度、阿曼和巴基斯坦的聚对苯二甲酸乙二醇酯树脂(PET)作出反倾销和反补贴肯定性初裁。 裁定结果如下:中国公司的倾销幅度为3.3%-17.4%,补贴幅度为22.8%,临时税率26.1%-40.2%;印度公司倾销幅度为34%-45.6%,补贴幅度为3.9%-31.1%,临时税率37.9%-76.7%;阿曼公司倾销幅度为22.2%-41.3%,补贴幅度为0.5%-4%,临时税率22.2%-45.3%;巴基斯坦公司倾销幅度为4 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |