牌号简介 About |
---|
D/W 203是一种非烧结的聚四氟乙烯(聚四氟乙烯)薄膜,主要用于电气绝缘,特别是电线和电缆应用。聚合物是纤维化的,在机器方向上具有很好的强度。它具有聚四氟乙烯固有的优点:优异的耐化学性,极端温度范围从450华氏度到+500华氏度,摩擦系数低,优异的悬垂特性和不粘特性。D/W 203用于电缆绝缘、线束缠绕以及同轴电缆的介质。一旦烧结,它完全密封,以提供优良的电气绝缘性能,无与伦比的耐化学性和优良的热阻。杜瓦尔的非烧结聚四氟乙烯带具有良好的悬垂特性,使其能够顺利地符合复杂的形状。D/W 203可用于垫圈、膨胀节、阀门密封和隔膜应用。它是可用的无色素和色素,以匹配环评的颜色。烧结后强度高,适用于需要化学惰性和耐高温的场合。 D/W 203 is an unsintered PTFE (Polytetrafluoroethylene) film used primarily for electrical insulation, particularly for wire and cable applications. The polymer is fibrilated giving good strength in the machine direction. It has the inherent benefits of PTFE: exceptional chemical resistance, extreme temperature range from 450F to +500F, low coefficient of friction, excellent drape characteristics and non-stick properties. D/W 203 is used in cable insulation, harness wrap, and as the dielectric medium in coaxial cables. Once sintered, it seals completely to provide excellent electrical insulating properties, unsurpassed chemical resistance and excellent thermal resistance. DeWAL's unsintered PTFE tape has good drape characteristics allowing it to conform smoothly to complicated shapes. D/W 203 can be used for gaskets, expansion joints, valve seals and diaphragm applications. It is available unpigmented and pigmented to match EIA colors. It has good strength after sintering and is used where chemical inertness and high temperature resistance are needed. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.50 | g/cm³ | |
Thickness Thickness |
50.8 到 508.0 | µm | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,51 µm MD, yield, 51 µ m |
12.4 | MPa | ASTM D882 |
MD,屈服,130 µm MD, yield, 130 µ m |
10.3 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
|||
MD,断裂 MD, fracture |
30 | % | ASTM D882 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
基底材料 Base material |
|||
Core ID Core ID |
cm | ||
Maximum Roll OD Maximum Roll OD |
mm | ||
Width Width |
mm |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
扬子石化乙烯安装新增液化气蒸发零碎技术改造项目
2018-12-18 经过3个多月的施工,扬子石化乙烯装置新增液化气蒸发系统技术改造项目近日投用,此举有效提高了液化气加工处理量,乙烯日产量达2300吨以上。 扬子石化烯烃厂1套乙烯装置原有一套液化气(LPG)蒸发系统,蒸发能力为40吨/小时。由于液化气中带水和重组分,蒸发系统运行能力下降,使原1套乙烯装置设计能力从40吨/小时降至34~36吨/小时。当液化气蒸发系统因结垢造成能力下降至一定程度被迫切出清理时,乙烯联合装置将不能以液化气作原料,影响乙烯产量及整个装置的物料平衡。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |