PULSE™ 6000 BG是一种PC/ABS树脂,提供热老化特性、低温冲击性能和高熔融强度的有趣组合。它的低MFR使制造复杂的吹塑零件成为可能。该产品的典型应用是吹塑扰流器、膝垫和座椅靠背。 PULSE™ 6000 BG is a PC/ABS resin offering an interesting combination of heat ageing characteristics, low temperature impact performance and high melt strength. Its low MFR enables manufacturing of complex blow molding parts. Typical applications for this product are Blow Molded Spoilers, knee bolsters and Seat Backs. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.13 | g/cm³ | ASTM D792 |
密度 Density |
1.13 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
260℃,5.0kg 260℃,5.0kg |
6.0 | g/10min | ISO 1133 |
260℃,5.0kg 260℃,5.0kg |
6.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.40 to 0.70 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2 | |
屈服 yield |
MPa | ISO 527-2 | |
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2 | |
屈服 yield |
% | ISO 527-2 | |
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus 2 , 3 |
MPa | ISO 178 | |
弯曲强度 bending strength 2 , 3 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-40℃ -40℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-40℃ -40℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/4A | ||
-40℃ -40℃ |
kJ/m² | ISO 180-4A | |
23℃ 23℃ |
kJ/m² | ISO 180-4A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ISO 306/A120 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~82℃ MD:-40~82℃ |
1/℃ | ASTM D696 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
3 3 points |
【新闻资讯】查看全部
大连商品交易所6日PP行情表
2021-12-06 搜料网资讯: 说明: (1)价格:元/吨 (2)成交量、持仓量:手(按双边计算) (3)成交额:万元(按双边计算) (4)涨跌=收盘价-前结算价 (5)涨跌1=今结算价-前结算价 大连商品交易所 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |