牌号简介 About |
---|
KetaSpire KT- 820 CF30是中等流动性、 30 %玻纤增强聚醚醚酮( PEEK)。 该树脂的强度和刚度高于未增强KetaSpire PEEK树脂。玻纤增强树脂赋予结构性产品更高的机械强度,特别是工作温度接近300℃时。 KetaSpire PEEK按照最行业最高标准加工,以兼具各种出色的性能为特征,包括优异的耐磨损性、一流的抗疲劳性、易于熔融加工、高纯度、优异的耐有机物、酸和碱等化学物质的性能。 这些特性使得它非常适合医疗保健、交通运输、电子、化学处理和其它工业用途。 -米色:KetaSpire KT-820 GF30 BG20 Black: KetaSpire KT-820 GF30 BK95 KetaSpire® KT-820 GF30 is a medium flow, 30% glass fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire® PEEK resin. Reinforcement also affords greater mechanical robustness in structural applications, particularly those with service temperatures approaching 300°C. KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of best-in-class fatigue resistance, ease of melt processing, high purity, and excellent chemical resistance to organics, acids, and bases. These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing, and other industrial uses. Beige: KetaSpire® KT-820 GF30 BG20 Black: KetaSpire KT-820 GF30 BK95 |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-- -- |
110 | J/m | ASTM D256 |
-- -- |
13 | kJ/m² | ISO 180 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-- -- |
960 | J/m | ASTM D4812 |
-- -- |
56 | kJ/m² | ISO 180 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
315 | ℃ | ASTM D648 |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-50~50℃ MD:-50~50℃ |
1/℃ | ASTM E831 | |
比热 specific heat |
DSC | ||
50℃ 50℃ |
J/kg/℃ | DSC | |
200℃ 200℃ |
J/kg/℃ | DSC | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1530 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
3 mm 3 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
20.30 mm 20.30 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,1 秒 Shore D, 1 second |
ASTM D2240 | ||
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
-- -- 5 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
屈服 yield 5 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/1A/5 | |
-- -- |
MPa | ASTM D638 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
-- -- |
% | ISO 527-2/1A/5 | |
-- -- 6 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
屈服 yield |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
剪切强度 shear strength |
MPa | ASTM D732 | |
泊松比 Poisson's ratio |
ASTM E132 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
熔体质量流动速率 Melt Flow Rate |
|||
400℃,2.16kg 400℃,2.16kg |
g/10min | ASTM D1238 | |
收缩率 Shrinkage rate 4 |
ASTM D955 | ||
MD:3.2 mm MD:3.2 mm |
% | ASTM D955 | |
TD:3.2 mm TD:3.2 mm |
% | ASTM D955 | |
吸水率 Water absorption rate |
|||
24hr 24hr |
% | ASTM D570 | |
熔体表观粘度 Apparent viscosity of melt |
|||
400℃,1000 sec^-1 400℃,1000 sec^-1 |
Pa·s | ASTM D3835 |
备注 |
---|
1 Passes 60s VB flame, smoke & toxicity requirements. |
2 一般属性:这些不能被视为规格。 |
3 5" x 0.5" x 0.125" |
4 0.20 in/min |
5 类型1A, 0.20 in/min |
【新闻资讯】查看全部
外卖面前的环境本钱:15天所用塑料袋可覆盖西湖
2016-05-17 随着互联网时代的到来,各类外卖类APP如雨后春笋般涌现,我们在享受便利、快捷的同时,却忽略了它给生态环境带来的巨大压力。日前,一媒体报道揭示了外卖背后的环境成本。其以三家外卖平台公布的订单数据计算得出结论:大约15天外卖所用塑料袋可覆盖一个西湖。 对此,中国城市建设研究院有限公司总工徐海云认为,相比于塑料袋的重量,从其面积来看更客观。“因为塑料袋比较薄,数量多时展开面积就会很大。而从外卖包装的重量来看其在所有包装消费中所占的比例,更容易看出外卖包装所处的地位和影响。” |
外卖面前的环境本钱:15天所用塑料袋可覆盖西湖 伴随着网络时代的来临,各种外卖类APP如如雨后春笋不断涌现,我们在享有便捷、便捷的另外,却忽视了它给生态环境保护产生的极大工作压力。日前,一新闻媒体表明了外卖身后的自然环境成本费。其以三家外卖服务平台发布的订单信息数据信息测算下结论:大概半个月外卖常用塑料袋可遮盖一个杭州西湖。 对于此事,全国城市基本建设研究所有限责任公司总工程师徐海云觉得,对比于塑料袋的净重,从其总面积看来更客观性。“由于塑料袋较为薄,总数多时投影面积便会非常大。而从外卖包裝的净重看来其在全部包裝消費中常占的占比,更非常容易看得出外卖包裝所在的影响力和危害。” 为研究外卖身后的废弃物回收利用难题,新闻记者对徐海云开展了访谈。 外卖身后的自然环境成本费:半个月常用塑料袋可遮盖杭州西湖 塑料垃圾归类回收利用应合乎市场的需求 在获知外卖废弃物给自然环境产生的极大危害后,群众陈女士的第壹反映是:要少叫外卖来适用环境保护。徐海云对于此事表明认同:废弃物由消費造成,消費由每一个人造成。每一个人都应当尊崇勤俭节约,不必盲目消费。 但也是有新闻人强调:社会发展针对“白色污染”的根源预防是不是拥有实质的改进?垃圾分类回收和收购 是不是保证了最好是?这种外在难题若不可以处理,仅仅号召大家少应用中式快餐,就只有是壹种壹厢甘愿的“社会道德恰当”,并非解决困难的方法。 确实,废弃物回收利用的难题,靠个人的能量是没法进行的,必须政府部门核心、全部社会发展共同奋斗。 徐海云告知新闻记者,塑料垃圾收购 应当包含两层面:壹层面是原材料利用,另壹层面是电力能源回收利用。原材料回收利用便是使塑料垃圾尽量地再度转换成塑胶产品,这些方面应当考虑到市场的需求。“但伴随着我国消费力的提升,中低端销售市场处在委缩情况,原材料利用市场需求比较有限。” 塑料垃圾能源回收利用,将要无法转换成原材料利用的塑料垃圾根据集中焚烧处理后开展余热回收利用。“这也完成了塑胶的回收利用。而集中焚烧处理,并不一定对废弃物开展严苛归类。” 徐海云觉得,废弃物回收利用要求真务实。“我们要激励垃圾分类回收,但要创建在实际的基本上,要合乎市场的需求。” 提议创建塑料垃圾收购 成本费补助 伴随着“互联网技术 ”发展趋势起來的,不但是外卖领域,也有物流行业。为何外卖、物流行业发展趋势这般迅速? “由于仍未考虑到包裝成本费难题。”徐海云说,外卖包裝、物流包装成本费很低,顾客基本上无需投入一切成本,所有都会由社会发展开展解决。 现阶段,由于废料塑料袋重量较轻、容积大,其收购 成本费很高,因此 日常废料塑料袋壹般没有人收。“假如要回收利用,大家应当创建废料塑料袋回收利用补助体制,赔偿回收利用必须的成本,这些花费还要由顾客付钱。实际补助信用额度是伴随着市场的需求而变化的。像转换成原材料利用时,很有可能必须补助0.5-一元;假如要进到垃圾处理站焚烧处理得话,很有可能只必须一些钱。”徐海云说。 来源于:我国塑料机械网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。