NYCOA纳米UFF NT-90-100是尼龙6基纳米复合材料,通过原位聚合制备10%的粘土负载,以实现最佳的纳米粘土剥离。NYCOA纳米UFF NT-90-100可根据最终应用情况定制任何特定粘度范围。与纯尼龙6相比,该等级的尼龙硬度提高了100%,与玻璃填充尼龙的硬度相当。此外,与纯尼龙6相比,对水、氧、二氧化碳和燃料的阻隔性能提高了大约80%。 NYCOA nanoTUFF™ NT - 90-100 is Nylon 6 based Nanocomposite with 10% clay loading made via in-situ polymerization for optimum nano-clay exfoliation. NYCOA nanoTUFF™ NT - 90-100 can be tailor-made to any specific viscosity range, depending upon the final application. This grade offers a 100% improvement in stiffness vs. neat Nylon 6, and is comparable in stiffness to a 20% glass-filled Nylon. In addition, barrier properties to water, oxygen, carbon dioxide, and fuel are improved approximately 80% vs. neat Nylon 6. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.16 | g/cm³ | ASTM D792 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
51.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
2.0 | % | ASTM D638 |
弯曲模量 Bending modulus 2 |
5520 | MPa | ASTM D790 |
弯曲强度 bending strength 2 |
140 | MPa | ASTM D790 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
6.4mm 6.4mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
熔融温度 Melting temperature |
℃ | DSC |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
【新闻资讯】查看全部
PVC行业末尾逐步淘汰落后产能
2016-06-08 近年来,由于经济下行压力较大,PVC行业产能过剩矛盾较大以及国内对高耗能、高污染的限制政策等影响下,pvc行业落后产能逐步开始淘汰。2013年国内PVC产能达到2477万吨的历史高位,随后几年新增产能大幅减少,落后产能逐步淘汰,PVC有效产能不断减少,截至2016年5月份国内PVC产能2176万吨,较2013年高点回落12.2%。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |