牌号简介 About |
---|
特性:低粘度基本产品应用:单丝、刷毛和牙刷的高回收率。其在热变形温度(熔点高出近40°C)下的优势超过了PA 12。拉伸和弯曲强度在高湿强度下的显著回收。维斯塔的PA 612化合物因此,Mid D系列产品代表了特殊产品,是对Vestamid L系列PA 12化合物综合选择的补充。 Characterization: low-viscosity base product Applications: monofilaments, bristles with high recovery for paint brushes and tooth brushes Its advantages over PA 12 exhibit in the heat deflection temperature (melting point nearly 40 °C higher) tensile and flexural strength outstanding recovery at high wet strength The PA 612 compounds of the VESTAMID® D series consequently represent specialty products that complement the comprehensive selection of PA 12 compounds of the VESTAMID® L series. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.06 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate 2 |
ISO 294-4 | ||
TD TD |
1.0 | % | ISO 294-4 |
MD MD |
1.4 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
2.6 | % | ISO 62 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
1.0 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/1A | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/1A | |
屈服 yield |
% | ISO 527-2/1A | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 179/1eA | |
23℃,完全断裂 23 ℃, completely fractured |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ISO 75-2/B | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
0.45 MPa,未退火 0.45 MPa, unannealed 3 |
℃ | ISO 75-2/B | |
热变形温度 Hot deformation temperature |
ISO 75-2/A | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed 7 |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/B | |
熔融温度 Melting temperature 5 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index 5 |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
电解腐蚀 Electrolytic corrosion |
IEC 60426 | ||
ISO Shortname ISO Shortname |
ISO 1874 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 specimen 127x12.7x3.2 mm processing acc. to ISO 1874-2 |
3 after conditioning at 180 °C / 60 min |
4 2nd Heating |
5 50 drops Value |
【新闻资讯】查看全部
吉林经开区推进精密化工产业
2016-03-11 春节刚过,吉林经开区总投资超30亿元的吉林康乃尔公司60万吨甲醇制烯烃项目便紧锣密鼓地推进。这是吉林经开区今年实施的50项投资5000万元以上项目中的重中之重,也是推进精细化工产业补齐“短板”的重大举措。 乙烯、丙烯被称为化工的“粮食”。目前,经开区精细化工产业本身发展就出现了“缺粮”,严重制约了化工产业的发展。尤其是乙烯、丙烯两种原料易燃易爆,运输半径受限,依靠外购无法有效弥补化工产业原料短缺这块“短板”。 经过充分论证,吉林经开区精细化工龙头企业――吉林 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |