| 牌号简介 About |
|---|
| Capilene Tu 75 AV是一种控制流变的聚丙烯异相共聚物，用于注塑成型。Capilene Tu 75 AV的特点是：流变性可控，成核和抗静电添加剂，即使在低温下也具有优异的冲击强度，高流动性，成型周期短，尺寸稳定性好。适用范围：重型技术部件、冷冻食品包装、货架、橱柜、花园家具、长流程产品、桶和工具箱。 CAPILENE® TU 75 AV is a controlled rheology polypropylene heterophasic copolymer intended for injection molding. CAPILENE® TU 75 AV features: controlled rheology, nucleating and antistatic additives, excellent impact strength even at low temperature, high flow, short molding cycle time and good dimensional stability. Applications CAPILENE® TU 75 AV is suitable for: heavy duty technical parts, frozen food packaging, shelves, cabinets, garden furniture, products with long flow length, pails and toolboxes. |
产品描述 Product Description
用途：桶;食品包装;家具;工具/零件箱;
加工条件：注射成型 Injection Molding
性能特点： 成核的; 抗静电; 抗冲共聚物; 可控流变; 尺寸稳定性好; 耐低温冲击; 流动性高; 冲击性能好; High impact resistance,Good Dimensional Stability,High liquidity,Controllable rheological,Nucleation,Antistatic property,low-temperature impact resistance,Impact copolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
35 | g/10min | ASTM D1238 |
|
230℃，2.16kg 230℃，2.16kg |
35 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
屈服 yield 2 |
18.0 | MPa | ASTM D638 |
|
屈服 yield |
18.0 | MPa | ISO 527-2/50 |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield 2 |
8.0 | % | ASTM D638 |
|
屈服 yield |
% | ISO 527-2/50 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲模量 Bending modulus 3 |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
-20℃ -20℃ |
J/m | ASTM D256 | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180 | ||
|
-20℃ -20℃ |
kJ/m² | ISO 180 | |
|
23℃ 23℃ |
kJ/m² | ISO 180 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 2,0 in/min |
| 3 0,20 in/min |
| 4 压 力1 (10N) |
|
【新闻资讯】查看全部 
万华化学HCl循环技术入围Chemical Week 2021可持续发展最佳循环实践
2021-12-05 搜料网资讯： 近期，美国Che mica l Week 2021年可持续发展奖项揭晓， 万华 化学HCl绿色循环技术入围最佳循环实践案例，这也是中国企业首次入围该奖项。 万华化学创新性HCl 催化氧化 技术 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付