牌号简介 About |
---|
澳大利亚利安德巴塞尔公司的聚丙烯级EP301G是一种具有常规分子量分布的低流动冲击共聚物,采用通用添加剂包装配制而成。EP301G是专为挤出和吹塑应用而设计的,要求在低零件重量下具有良好的熔融强度和冲击强度。最终用途产品通常由EP301G制成,包括吹塑制品、挤压板、瓦楞纸板和挤压型材。 LyondellBasell Australia's Polypropylene grade EP301G is a low flow impact copolymer with a conventional molecular weight distribution and is formulated with a general-purpose additive package. EP301G is designed for extrusion and blow-moulding applications requiring good melt strength and good impact strength at low part weight. End use products typically made from EP301G include blow-moulded articles, extruded sheet, corrugated board and extruded profiles. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ISO 1183/D |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
1.2 | g/10min | ISO 1133 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-20℃ -20℃ |
4.0 | kJ/m² | ISO 180-1A |
0℃ 0℃ |
6.5 | kJ/m² | ISO 180-1A |
23℃ 23℃ |
15 | kJ/m² | ISO 180-1A |
跌落标靶冲击 Falling target impact |
|||
-40℃ -40℃ |
J | BS 2782 306B | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
同德化工2021年第一季度净利润约1930万元
2021-05-03 搜料网资讯: 4月26日晚间,同德化工披露2021年第一季度报告,报告期内,公司实现营业收入1.60亿元,同比增长98.68%;归属于上市公司股东的净利润1930.35万元,同比增长1184.12%;归属于 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |