牌号简介 About |
---|
环氧树脂红色是一种触变性环氧凝胶涂层,广泛用于手工层压/工具应用。它是一种坚韧的表面涂层树脂,在室温下固化,具有优异的耐磨性。环氧树脂涂料红色易于使用,能很好地润湿各种表面,在垂直表面上不会出现下垂。当环氧树脂在室温下变得“粘硬”后,玻璃纤维布在表面涂层的后面用环氧树脂层压而成,以产生具有良好尺寸稳定性和表面光洁度的坚固、轻量的工具。表面精密固化机,无缺口。应用范围包括精密工装、母版和模型制作、芯盒和夹具。 EpoxAcoat® RED and EpoxAcoat® GREY are thixotropic epoxy gel coats which are widely used for hand laminating/tooling applications. They are tough and strong surface coat resins which cure at room temperature and offer exceptional abrasion resistance. EpoxAcoat® RED and EpoxAcoat® GREY are easy to use, wet out well over a variety of surfaces and will coat vertical surfaces without sagging. After the epoxy becomes "tacky-hard" at room temperature, fiberglass cloth is laminated behind the surface coat using Free Form® AIR putty or EpoxAmite® Laminating Epoxy to produce strong, lightweight tools that have excellent dimensional stability and surface finish. Cured surface machines precisely without chipping. Applications include precision tooling, master and pattern making, core boxes and fixtures. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.49 | g/cm³ | ASTM D1475 |
特定体积 Specific volume |
0.668 | cm³/g | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.015 | % | ASTM D2566 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
混合比 Mixing ratio |
5A:1B by volume 100A:15B by weight | ||
Tack-up Time - Thin Film - Recoat Tack-up Time - Thin Film - Recoat |
1.0 | hr | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
巴氏硬度 Babbitt hardness |
ASTM D2240 | ||
拉伸强度 tensile strength 2 |
|||
断裂,23℃ Fracture, 23 ℃ 2 |
MPa | ASTM D638 | |
弯曲强度 bending strength 2 |
|||
23℃ 23℃ 2 |
MPa | ASTM D790 | |
压缩强度 compressive strength 2 |
|||
23℃ 23℃ 2 |
MPa | ASTM D695 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
储存稳定性 storage stability |
min | ASTM D2471 | |
脱模时间 stripping time 3 |
min | ||
Tack Free Time(Thin Film) Tack Free Time(Thin Film) |
hr | ||
工作时间 working hours |
|||
Thin Film Thin Film |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 6 ply / 10 oz. laminate after 7 days at 73° F. / 23° C. |
3 Cure Time |
【新闻资讯】查看全部
凯盛新材IPO注册生效,募资建设2000吨/年聚醚酮酮树脂项目
2021-08-13 搜料网资讯: 8月11日,华邦生命健康股份有限公司控股子公司凯盛新材IPO注册生效,同时公开《首次公开发行股票并在创业板上市招股说明书》。 据天眼显示,凯盛新材成立于2005年, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |