牌号简介 About |
---|
伊士曼TrTIN共聚酯TX1801是专门开发用于吹塑成型应用的非晶共聚酯。伊士曼TrTIN共聚酯TX1801含有从植物源衍生的脱模剂。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化学性。此外,这一新一代共聚酯具有良好的外观和清晰度。伊士曼TrTIN共聚酯TX1801可用于美国食品和药物管理局(FDA)的重复使用食品接触物品。 Eastman Tritan™ Copolyester TX1801 is an amorphous copolyester specifically developed for use in blow molding applications. Eastman Tritan™ Copolyester TX1801 contains a mold release derived from vegetable based sources. Its most outstanding features are excellent toughness, hydrolytic stability, heat resistance, and chemical resistance. In addition, this new generation copolyester offers excellent appearance and clarity. Eastman Tritan™ Copolyester TX1801 may be used in repeated use food contact articles under United States Food and Drug Administration (FDA) regulations. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.18 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.60 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180 | ||
23℃ 23℃ |
840 | J/m | ASTM D256 |
23℃ 23℃ |
No Break | ASTM D4812 | |
-40℃ -40℃ |
12 | kJ/m² | ISO 180 |
23℃ 23℃ |
kJ/m² | ISO 180 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
-40℃,Energy at Maximum Load -40℃,Energy at Maximum Load |
J | ASTM D3763 | |
0℃,Energy at Maximum Load 0℃,Energy at Maximum Load |
J | ASTM D3763 | |
23℃,Energy at Maximum Load 23℃,Energy at Maximum Load |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance |
|||
总计 total |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
吹塑工艺和注塑工艺有什么区别?
2019-01-09 吹塑 产品都是中空的;注塑因为有注塑口,所以成型后的产品会多出一小快不要的部分,会有道工序把它剪掉,不过如果仔细观察还是可以发现的; 注射成型 是使热塑性或热固性模塑料 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |