牌号简介 About |
---|
D/W 200是从改性的均聚聚四氟乙烯树脂中剥离出来的,它含有比我们的220膜中更高水平的全氟化共聚单体。共聚单体的加入使材料的电性能和物理性能得到改善。这种薄膜可以热粘合(熔合)到自身(625-650华氏度)。改性均聚物树脂的耐化学性能与均聚物聚四氟乙烯相当。其拉伸强度比均聚聚四氟乙烯高约25%,延伸率比均聚聚四氟乙烯高约60%。由于这些特性,D/W 200通常是熔融可加工薄膜(如PFA)的良好替代品。D/W 200可热熔合至自身,使需要这些特性的结构的制造成为可能。D/W 200还可用作电气和电子电缆应用中的高介电强度易熔包。它也可作为电路板工业中的一种粘合膜。 D/W 200 is skived from a modified homopolymer PTFE resin containing a higher level of a fully fluorinated comonomer than is in our 220 film. The incorporation of the comonomer yields a material with improved electrical and physical properties. This film can be thermally bonded (fused) to itself (625 - 650 degrees F). The modified homopolymer resin exhibits chemical resistance equivalent to that of homopolymer PTFE. Its tensile strength is approximately 25% higher, and the elongation is approximately 60% higher than for homopolymer PTFE. Because of these properties D/W 200 is often a good substitute for melt Processable films such as PFA. D/W 200 may be thermally fused to itself making possible the fabrication of structures requiring these properties. D/W 200 can also be used as a high dielectric strength fusible wrap in electrical and electronic cable applications. It can also be used as a bonding film in the circuit board industry. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Thickness Thickness |
12.7 到 1574.8 | µm | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
MD,屈服 MD, yield |
41.4 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
|||
MD,断裂 MD, fracture |
500 | % | ASTM D882 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
连续使用温度 Continuous use temperature |
260 | ℃ | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
110 | kV/mm | ASTM D149 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
基底材料 Base material |
|||
Core ID Core ID |
cm | ||
Maximum Roll OD Maximum Roll OD |
mm | ||
Width Width |
mm |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
中科炼化成功生产太阳能光伏级EVA
2022-05-24 5月17日,中科炼化EVA(乙烯-醋酸乙烯共聚物)装置首次生产太阳能光伏料新产品,将有效缓解该产品依赖进口局面,有力推动合成树脂产品顶替进口工作。 近年来,随着国内光伏行业 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |