牌号简介 About |
---|
TOPAS® 9506F-500 TOPAS® 9506F-500是一种环烯烃共聚物 (COC)产品,。 它,在亚太地区有供货。 典型应用领域为:电影。 特性包括: 共聚物 加工性能良好 TOPAS®9506F-500 Product 说明:TOPAS 9506F-500是一种低玻璃过渡膜挤出共混级。它是一种中等透明度的树脂,具有高硬度、防潮性、耐化学性、热成型性和纯度,可用于食品和医疗保健领域。它用于单层混合铸造应用,以及在铸造和吹制过程中的共挤,用于各种薄膜和薄板产品。主要应用包括收缩膜和标签,在适当的温度下收缩是必要的。为了提高高温下的性能,提高TOPAS的玻璃化转变温度(Tg)等级 TOPAS® 9506F-500 TOPAS® 9506F-500 is a Cyclic Olefin Copolymer (COC) product. It is available in Africa & Middle East, Asia Pacific, or Latin America. Typical application: Film. Characteristics include: Copolymer Good Processability TOPAS® 9506F-500 Product Description TOPAS 9506F-500 is a low glass transition film extrusion blending grade. It is a medium clarity resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food applications. It is used in monolayer blended cast applications, and in coextrusions in both cast and blown processes, for a variety of film and sheet products. Leading applications include shrink film and labels where shrinkage at moderate temperatures is desired. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended. Selected Applications Shrink films and labels Thermoformed PE films Food packaging Food contact Leading Attributes High shrink, low stress, gloss, clarity, toughness Improved material distribution, stiffness, depth Not manufactured with BPA, phthalates, or halogens Broad regulatory compliance |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.01 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
190℃,2.16 kg 190℃,2.16 kg |
1.00 | cm³/10min | ISO 1133 |
230℃,2.16 kg 230℃,2.16 kg |
6.00 | cm³/10min | ISO 1133 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
0.010 | % | ISO 62 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
ISO 527-3 | ||
23℃ 23℃ |
2400 | MPa | ISO 527-2/1A/1000 |
MD,23℃ MD,23℃ |
MPa | ISO 527-3 | |
TD,23℃ TD,23℃ |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,23℃ MD, fracture, 23 ℃ |
MPa | ISO 527-3 | |
TD,断裂,23℃ TD, fracture, 23 ℃ |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,23℃ MD, fracture, 23 ℃ |
% | ISO 527-3 | |
TD,断裂,23℃ TD, fracture, 23 ℃ |
% | ISO 527-3 | |
水蒸气渗透性 water vapor permeability 2 |
|||
38℃ 38℃ 2 |
g·100µm/(m²·day | ISO 15106-3 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature 3 |
℃ | ISO 11357-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 90% RH |
3 10°C/min |
【新闻资讯】查看全部
滨州市废塑料回收使用体系建设现场推进会议召开
2018-04-28 4月25日,滨州市废塑料回收利用体系建设现场推进会议召开,副市长曹玉斌出席会议。 据了解,依据《关于推进全市废塑料回收利用体系建设的实施意见》,滨州市将利用3年左右的时间,以“两体系一园区”(即废塑料回收体系、分拣体系和高值化利用园区)标准化建设为载体,以龙福环能科技股份有限公司等龙头企业为主体,先行先试,建成全方位覆盖人流量密集区域,辐射全省的“互联网+废塑料”模式的高效回收利用体系。同时,将积极开展废塑料回收利用循环经济标准化试点,开展商业模式创新,建立废塑料回收利用集 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |