| 牌号简介 About |
|---|
| Lexan Lux9612g树脂Lexan Lux9612g（Exrl0945）是一种紫外线稳定的高粘度阻燃聚碳酸酯，具有无溴、无氯化的FR体系，具有扩散效应和薄壁FR性能，在热暴露下具有良好的颜色稳定性。为LED应用开发。满足各种用途的WEEE/ROHS要求。 Lexan LUX9612G is a UV stabilized high viscosity, flame retardant polycarbonate featuring non brominated and non chlorinated FR system with diffusion effect and thin wall FR performance providing good colorstability under heat exposure. Developed for LED applications. It meets WEEE/RoHS requirements for various applications. |
产品描述 Product Description
用途：发光二极管;薄壁部件;
加工条件：注射成型 Injection Molding
性能特点： 无卤; 防火阻燃等级V-0; 高粘度; 颜色稳定; 阻燃; 耐候抗UV; Weather resistance is good,High Viscosity,Halogen free,Flame Characteristics,Good color stability,V-0
紫外线：UV Stabilized
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.20 | g/cm³ | ASTM D792 |
|
密度 Density |
1.20 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，1.20kg 300℃，1.20kg |
7.0 | g/10min | ASTM D1238 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
300℃，1.2 kg 300℃，1.2 kg |
7.00 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.2 mm MD：3.2 mm |
0.60 to 0.80 | % | 内部方法 |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
% | ISO 62 | |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength 3 |
|||
|
断裂 fracture |
MPa | ISO 527-2/50 | |
|
断裂 fracture 3 |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
屈服 yield 3 |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2/50 | |
|
断裂 fracture 4 |
% | ASTM D638 | |
|
屈服 yield 3 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/50 | |
|
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
|
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
|
弯曲强度 bending strength 6 , 7 |
MPa | ISO 178 | |
|
弯曲强度 bending strength 4 |
|||
|
屈服，50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ 8 |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
|
23℃，Total Energy 23℃，Total Energy |
J | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature 9 |
|||
|
1.8 MPa，未退火，64 mm跨距 1.8 MPa, unannealed, 64 mm span 9 |
℃ | ISO 75-2/Af | |
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
0.45 MPa，未退火，64 mm跨距 0.45 MPa, unannealed, 64 mm span 9 |
℃ | ISO 75-2/Bf | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 10 | |
|
球压测试 Ball pressure test |
|||
|
125℃ 125℃ |
IEC 60695-10-2 | ||
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD：-40~40℃ TD：-40~40℃ |
1/℃ | ASTM E831 | |
|
MD：-40~40℃ MD：-40~40℃ |
1/℃ | ASTM E831 | |
|
相对温度指数 Relative temperature index |
|||
|
电气性能 Electrical performance |
℃ | UL 746 | |
|
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
|
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
|
高电弧燃烧指数（HAI） High Arc Burning Index (HAI) |
UL 746 | ||
|
热丝引燃 Hot wire ignition |
|||
|
HWI HWI |
UL 746 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
|||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
灼热丝可燃性指数 Glowing wire flammability index |
|||
|
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
|
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
|
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0.20 in/min |
| 3 类型 1, 2.0 in/min |
| 4 0.051 in/min |
| 5 0.079 in/min |
| 6 0.49 in/min |
| 7 Break |
| 8 80*10*3 |
| 9 80*10*4 mm |
| 10 标准 B (120°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部
镇海炼化聚乙烯下料阀攻关获得新打破
2017-06-28 6月22日，历时近3天的改造，化工部聚乙烯装置A1线产品下料E阀于上午成功投运，阀门开关速度从原来8秒提高到4秒，满足了程序控制要求，聚乙烯装置产品下料阀长周期运行攻关取得新的突破。 聚乙烯装置产品下料阀自2009年投运至今已运行8年时间，在此期间阀门执行机构出现过各种故障。8年来，仪控部组织过多次攻关和改造，执行机构的使用寿命有所增长，但目前设备性能下降严重、功能配置已不能满足目前工况运行要求，严重制约装置长周期运行。为此，仪控部持续进行攻关，制定改造方案，认真做好执行机 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付