牌号简介 About |
---|
LARIPUR® LPR 2203-93A是一种热塑性聚氨酯弹性体(聚醚)(TPU-聚醚)材料,。 该产品在北美洲、拉丁美洲或欧洲有供货,加工方式为:注射成型。 LARIPUR® LPR 2203-93A的主要特性有: 耐候性好 耐化学品 耐磨 PRODUCTS FOR GASKETS These are specially developed TPUs for manufacturing hydraulic gaskets or any other application where at high compression set, resistance to oils and/or high temperatures, is required. Two products based on polycaprolactone (2202-95A and 107- 93A) plus one based on Ether (2203-93A) belong to this group depending on the application. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.14 | g/cm³ | DIN 53479 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
DIN 53504 | ||
50% 50% |
9.00 | MPa | DIN 53504 |
100% 100% |
11.2 | MPa | DIN 53504 |
300% 300% |
21.4 | MPa | DIN 53504 |
拉伸强度 tensile strength |
|||
断裂 fracture |
51.1 | MPa | DIN 53504 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | DIN 53504 | |
撕裂强度 tear strength |
N/mm² | DIN 53515 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
压缩形变 Compression deformation |
|||
23℃,70 hr 23℃,70 hr |
% | DIN 53517 | |
70℃,22 hr 70℃,22 hr |
% | DIN 53517 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
DIN 53505 | ||
弯曲模量 Bending modulus |
ISO 178 | ||
磨损量 Wear amount |
mm³ | DIN 53516 | |
撕裂阻力 Tear resistance |
MPa | DIN 53515 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
季君晖、卢波:外卖“大迸发”,净化触目惊心
2017-06-23 近年来,互联网外卖市场的蓬勃发展给人们生活带来了极大便利,但随之而来外卖包装的大量产生对环境造成了很大负担。 根据比达咨询发布的《2016年中国第三方餐饮外卖市场研究报告》,2016年我国外卖单笔消费16-20元的用户最多,占比33.6%,单笔消费11-30元的用户占到83.1%。在以上数据基础上进行假设,平均每单消费是20元,那么2018年总共将有330亿单,每单外卖包装平均约为70g,2018年消耗掉的外卖包装大约为231万吨。 外卖包装主要包括餐盒、餐 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |