牌号简介 About |
---|
VIPEL F701-S系列树脂是高分子量、两级间苯二甲酸、不饱和聚酯树脂,具有通用树脂的润湿、固化和搬运特性。主要特点是苯乙烯含量较低。他们有极好的保质期,是理想的纤维缠绕和喷涂。下面列出了一些选定的树脂。优点耐腐蚀AOC的Vipel F701-S系列树脂在与无机和有机酸接触时具有优异的耐腐蚀性。许多石油产品,如煤油、加热油和原油,耐溶剂性已得到现场验证。请参阅AOC的“耐腐蚀树脂指南”,了解耐腐蚀信息或关于树脂是否适合任何特定化学环境的问题。F701-S系列树脂的苯乙烯含量低于标准版本。用途广泛,适用于手工制作、喷涂、纤维缠绕等多种制造方法。 Vipel® F701-S Series resins are high molecular weight, two-stage isophthalic, unsaturated polyester resin with the wet out, cure and handling characteristics of general purpose resins. The main feature is lower styrene content. They have an excellent shelf life and are ideal for filament winding and spray-up. A few selected resins are listed below. BENEFITS Corrosion resistance AOC's Vipel® F701-S series resins provide excellent corrosion resistance when used in contact with inorganic and organic acids. Solvent resistance is field-proven for many petroleum products such as kerosene, heating oil and crude oils. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC. F701-S series resins contain less styrene than standard versions. Versatile Suitable for various fabricating methods such as hand lay-up, spray-up and filament winding. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
苯乙烯含量 styrene content |
42 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
128 | ℃ | ISO 75-2/A |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Gel to Peak Gel to Peak |
13.0 | min | |
放热峰值 exothermic peak |
193 | ℃ | |
触变指数 Thixotropic index 2 |
2.10 | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ||
粘度 viscosity |
|||
布络克菲尔德 RVT,25℃ 25℃,Brookfield RVT |
Pa·s | ||
胶凝时间 Gelation time |
|||
25℃ 25℃ |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
巴氏硬度 Babbitt hardness |
ISO 75-2/A | ||
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2/20 rpm |
【新闻资讯】查看全部
PEEK聚合物让眼镜减负
2016-11-09 轻量化在汽车行业得到众多关注,而这一技术也让其他行业产品受益。最近的一个应用就是眼镜。香港Mentor光学有限公司推出Plasteel系列眼镜,仅仅重9克,而不是通常的23克。 赢创 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |