牌号简介 About |
---|
Clearflex® CH D0是一种线性低密度聚乙烯,含有抗氧化剂,以极低密度(VLDPE)为特征。该树脂具有很高的拉伸性能和最佳的粘附效果。主要应用Clearflex® CH D0推荐用于需要软接触和柔韧性的应用,以提高抗冲击性,当作为添加剂与其他聚烯烃混合时,使用或不使用矿物填料。Clearflex® CH D0还用作拉伸膜中的粘着剂。 Clearflex CH D0 is a linear low density polyethylene, with antioxidants, characterised by a very low density (VLDPE). The resin has a high stretchability and an optimum cling effect. Main Application Clearflex CH D0 is recommended for applications in which soft touch and flexibility are required, for improvement of impact resistance when used as additive in blend with other polyolefins formulated with or without mineral fillers. Clearflex CH D0 is also used as cling agent in stretch film. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
与自身 - 动态,铸造薄膜 With oneself - dynamic, casting thin films |
> 0.50 | ISO 8295 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
8 to 50µm | ||
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,铸造薄膜 1% secant, MD, cast thin film |
50.0 | MPa | ISO 527-3 |
1% 正割,TD,铸造薄膜 1% secant, TD, cast thin film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,吹塑薄膜 MD, yield, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,吹塑薄膜 TD, yield, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,吹塑薄膜 MD, fracture, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,吹塑薄膜 TD, fracture, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,挤塑薄膜 MD, fracture, extruded film |
% | ISO 527-3 | |
TD,断裂,挤塑薄膜 TD, fracture, extruded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact 2 |
|||
铸造薄膜 Casting thin film 2 |
g | ISO 7765-1/A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 3 |
ISO 6383-2 | ||
MD MD |
kN/m | ISO 6383-2 | |
TD TD |
kN/m | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,铸造薄膜 45 °, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
铸造薄膜 Casting thin film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
3 Cast Film |