牌号简介 About |
---|
TPX® MX002 TPX® MX002是一种聚甲基戊烯共聚物(PMP 共聚物)材料,。 该产品在北美洲有供货,加工方式为:吹塑成型、型材挤出成型、挤出、挤出涂层、注射成型、管路挤出成型或纤维(纺纱)挤出。 TPX® MX002的主要特性为:良好的刚度。 TPX® MX002 TPX® MX002是一种聚甲基戊烯共聚物(PMP 共聚物)材料,。 该产品在亚太地区或欧洲有供货,加工方式为:吹塑成型、挤出或注射成型。 TPX® MX002的主要特性为:坚硬。 TPX™ MX002 TPX™ MX002 is a Polymethylpentene Copolymer (PMP Copolymer) material. It is available in North America for blow molding, extrusion, extrusion coating, fiber (spinning) extrusion, injection molding, pipe extrusion, or profile extrusion. Primary attribute of TPX™ MX002: Good Stiffness. TPX™ MX002 TPX™ is a 4-methylpentene-1-based olefin copolymer. TPX™ has a unique molecular structure. Although TPX™ is a crystalline olefin polymer, it shows transparency. Because of its excellent heat-resistance, release property and chemical resistance, TPX™ is used for industrial materials, including mandrels and sheaths in the manufacture of high-pressure rubber hose, mold cups to create LED light and other applications such as release film on FPC manufacturing process and release paper in the manufacture of synthetic leather. Furthermore, TPX™ possesses a lowest density among thermoplastic polymers and then provides the molded articles with lower weight. This leads to reduce the environmental load for transportation. It is also noted that TPX™ is a halogen-free polymer denoted as environmentally-friendly material. TPX™ is also used for food-related applications such as food wraps, food preservation packs, baking carton and microwave oven tableware. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.83 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
1.5 | % | ASTM D995 |
TD TD |
1.1 | % | ASTM D995 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.01 | % | ASTM D570 |
熔体质量流动速率 Melt Flow Rate |
|||
260℃,5.0kg 260℃,5.0kg |
21 | g/10min | ASTM D1238 |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
雾 度 μm Haze μ M |
% | ASTM D1003 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
熔融温度 Melting temperature |
℃ | ASTM D4591 | |
维卡软化温度 Vicat Softening Temp |
|||
|
℃ | ASTM D1525 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻 Volumetric resistance |
Ω.cm | ASTM D257 | |
绝缘强度 Insulation strength |
|||
|
KV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
23℃ 23℃ |
1 MHz | ASTM D150 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50mm 1.50mm |
UL-94 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
R 级 | ASTM D785 | |
拉伸强度 tensile strength |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 模具温度: 163°F, 熔体温度: 590°F |
3 260 to 280°C |
4 类型 4, 2.0 in/min |
5 0.051 in/min |
6 120°C/hr |
7 速率 A (50°C/h), 压 力1 (10N) |
8 Injection Molded |
9 Injection Molded, 2 mm, 589 nm wavelength |
【新闻资讯】查看全部
巴斯夫公司高层指导实地观赏考察德纳国际南京工厂
2016-09-12 BASF全球建材和乙氧基化采购总监Beate Salvador女士和Heinz FriedrichS utoris先生、上海巴斯夫亚太区采购经理华正亮先生和周震先生,莅临德纳国际南京工厂进行实地参观考察和访问,德纳国际总裁秦旭东代表公司对巴斯夫公司的到来表示热烈欢迎,并安排了细致的接待工作,陪同的人员还有南京公司总经理孙家兴、营销副总裁余科峰、技术副总裁杨建国、市场总监梁甫军、外贸部经理刘潇潇。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |