牌号简介 About |
---|
具有无孔ESTAR共聚酯6763皮的Ethalalt发泡共聚酯MP07F是一种透明的无定形材料,具有封闭的泡沫结构,可用于医疗包装。它通常是白色/珠光的外观,但也可以使用伊士曼树脂和浓缩物着色。应用/使用医疗包医疗安装卡不透明医疗和药物包装热成型包装工作在工艺托盘中关键属性可与其他共聚酯回收用于非医疗消费后市场,环氧乙烷(ETO)、γ或电子束辐照或气体等离子体ST后的颜色和功能稳定性。符合ISO 11607适用章节的灭菌,包括微生物屏障,符合ISO 10993医疗器械生物相容性要求,缩短热成型周期和能源使用,设计更灵活,包括耐久性、易印刷、深咬边、长寿命铰链、增强的产品保护G。比其他材料(包括乳胶、丁二烯、双酚S(BPA)和双酚S(BPS)、邻苯二甲酸酯、PVC、卤素等)更易受脆裂影响的HIPS更易发生撕裂和弯曲强度,更轻的阻光和不透明度,更轻的无苯乙烯替代品符合环保的采购指南,零件的最小生成量。修剪或切割时的绞刀和天使毛发最小应力美白为共聚酯使用的普通盖面材料提供了良好的热密封性能。COF和阻断力控制不需要进行表面改性。可持续LCA-每个托盘的全球变暖潜力为0.33千克二氧化碳当量/托盘,使用MP007F隔热材料制成。影响 Eastalite™ Foamed Copolyester MP007F with nonporous Eastar™ Copolyester 6763 skins is an opaque, amorphous material with a closed foam structure useful for medical packaging. It is normally white/pearlescent in appearance but may also be colored using Eastman resins and concentrates. Application/Uses Medical kits Medical mounting cards Opaque medical and pharmaceutical packaging Thermoformed packaging Work-in-process trays Key Attributes Can be recycled with other copolyesters for use in nonmedical post-consumer markets Color and functional stability following ethylene oxide (EtO), gamma or e-beam irradiation, or gas plasma sterilization Compliant with applicable sections of ISO 11607 including microbial barrier Complies with select ISO 10993 requirements for biocompatibility of medical devices Decreased thermoforming cycle time and energy use Greater design flexibility including durability, easy printing, deep undercuts, long-life hinges, enhanced product protection Greater tear and flex strength than more brittle and crack susceptible HIPS Light blocking and opacity Light weight Styrene-free alternative Made without other materials of concern, including Latex, Butadiene, BPA and bisphenol S (BPS), ortho-phthalates, PVC, halogens Meets environmentally preferable purchasing guidelines Minimal generation of particulates and angel hair when trimmed or cut Minimal stress whitening Provides good heat seal performance to common lidding materials used with copolyesters Surface modifications are not necessary for COF and blocking force control Sustainable LCA -The global warming potential per tray is 0.33 kg CO2-eq/tray made using MP007F Temperature insulating effect |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.778 | g/cm³ | ASTM D792 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
ASTM D374 | ||
-- -- 2 |
60 | µm | |
-- -- 3 |
1000 | µm | |
弹性模量 Elastic modulus |
|||
TD TD |
639 | MPa | ASTM D882 |
MD MD |
691 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
MPa | ASTM D882 | |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
MD,断裂 MD, fracture |
MPa | ASTM D882 | |
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,屈服 MD, yield |
% | ASTM D882 | |
TD,屈服 TD, yield |
% | ASTM D882 | |
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
Graves Tear Graves Tear |
ASTM D1004 | ||
MD MD |
kN/m | ASTM D1004 | |
TD TD |
kN/m | ASTM D1004 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
Max Load Max Load |
N | ASTM D3763 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
不透明 Opaque |
% | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Thickness of Each Eastar™ Copolyester Skin Layer |
3 Total Thickness of A/B/A Sheet Tested |
【新闻资讯】查看全部
【干货】你知道吗?提高模具质量的十大因素
2021-03-25 搜料网资讯: 模具制造过程是是一个复杂的过程,从设计、加工、装配、调试等步骤,最后才能真正地投入使用,在整个生命周期中,影响模具质量的因素主要有以下十个方面: 1.模具 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |