| 牌号简介 About |
|---|
| Bormed™ TD109CF是一种丙烯-α-烯烃共聚物。适用于冷辊法无取向铸膜、管式水淬法吹膜及BOPP薄膜的生产。 Bormed TD109CF is a propylene alpha olefin copolymer. This grade is suitable for the manufacturing of non-oriented cast films on chill roll process and blown films on tubular water quenching process. CAS-No.: 25895-47-0 Applications Bormed TD109CF has been evaluated according to different regulations and norms. Typical applications are mentioned below for Medical devices or Pharmaceutical & Diagnostic packaging. However, Borealis should be consulted for final approval to evaluate the use of Bormed TD109CF . Medical device packaging Pouches for IV solutions This grade may only be used for the applications listed in the Product Datasheet and only to the extent that the application is within the scope of the tests set out in the Statement on Compliance to Regulations on Medical Use for that grade. If an application is not listed in the Product Datasheet, the grade can be used for such application only after express written consent of the Borealis Marketing Manager, Healthcare. Borealis prohibits the use of any healthcare grade product in an implantable device that is introduced into the human body by surgical intervention and that is intended to remain in place following surgical procedure. Special features Excellent optical properties Wide sealing window Low sealing initiation temperature Sterilisability by means of water steam High seal strength and hot tack force |
产品描述 Product Description
用途：薄膜;流延薄膜;医用包装;
加工条件：吹塑薄膜
性能特点： 耐低温热封性; 透湿性差; 蒸汽消毒; 共聚物; 热粘性强; 密封范围宽; 光学性能; 热封性好; Good heat sealing,Steam sterilized,Optical performance,Thermal viscous strength,Poor moisture permeability,Broad Seal Range,Copolymer,Low temperature heat sealing
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
6.0 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
弯曲模量 Bending modulus |
|||
|
23℃，注塑成型 23 ℃, injection molding |
700 | MPa | ISO 178 |
|
摩擦系数 friction coefficient |
|||
|
与自身 - 动态 With oneself - dynamic |
> 0.70 | ISO 8295 | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
ISO 527-3 | ||
|
MD，50 µm MD，50 µm |
470 | MPa | ISO 527-3 |
|
TD，50 µm TD，50 µm |
490 | MPa | ISO 527-3 |
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
MD，50 µm MD，50 µm |
MPa | ISO 527-3 | |
|
TD，50 µm TD，50 µm |
MPa | ISO 527-3 | |
|
拉伸应变 Tensile strain |
ISO 527-3 | ||
|
MD，断裂，50 µm MD, fracture, 50 µ m |
% | ISO 527-3 | |
|
TD，断裂，50 µm TD, fracture, 50 µ m |
% | ISO 527-3 | |
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
|
50 µm，Total Energy 50 µm，Total Energy |
J | ISO 7765-2 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
20°，50 µm 20°，50 µm |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
50 µm 50 µm |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部
利安德巴塞尔工厂遭遇不可抗力
2016-10-14 在周二发布的客户通知书中，利安德巴塞尔宣布其位于德克萨斯州的拉波特工厂以及位于伊利诺依州的莫里斯工厂因遭遇不可抗力而受到影响。 据早期的记录显示，事件起因可追溯至5月17日。当时两州工厂的线性低密度聚乙烯生产装置均出现了设备问题。 目前，利安德巴塞尔并未就此事发表更多评论。 拉波特工厂和莫里斯工厂的线性低密度聚乙烯年产能分别为355,166吨以及295,292吨。 普氏能源资讯于周一对线性低密度聚乙烯(丁烯)价格进行了评估，到 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付