牌号简介 About |
---|
成型纬度宽,刚性好,易磨性好,丁烯共聚物 Description UR654 is a butenecopolymer produced via Unipol process tecnology and suitable for rotational molding. Broad molding latitude Good Grindability Good Color stability & ESCR Excellent stiffness Applications Rotational molding(Storage container) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.938 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.2 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
F50 F50 |
> 300 | hr | ASTM D1693 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
17.7 | MPa | ASTM D638 |
断裂 fracture |
24.5 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
巴斯夫更新TDI事情声明:估计不会造成健康危害
2017-10-16 作为风险评估的一部分,巴斯夫专家对德国路德维希港8月25日至9月29日期间生产的TDI制成的泡沫进行了初步试验,结果及后续计算显示不会造成健康危害。巴斯夫将向相关主管部门和协会提供详细评估信息。关于路德维希港生产的TDI产品出现质量波动问题,经巴斯夫确认受影响的材料并未直接销往亚洲。亚洲地区的TDI生产装置未受波及,未发现同类质量问题。 在 7500 吨二氯苯值较高的甲苯二异氰酸酯 (TDI) 中,近三分之二尚未进一步加工。巴斯夫已经与客户合作启动了产品召回流程。约 75 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |