牌号简介 About |
---|
一种硅烷接枝交联聚乙烯化合物,可在潮湿条件下固化,用于电力电缆绝缘,在高输出速率下具有优异的挤出性。PP 409是专门为高达72千伏的电缆开发的。使用的特殊配方和复合技术确保污染水平保持在该电压等级所需的限值内。PP 409的一般熔融指数范围为0.7-1.0,在挤压过程中提供了稳定的稳定性,特别是对于高压所需的厚绝缘。说明:该化合物利用道康姆(Dow Coming)开发的被称为Sioplas的聚乙烯交联体系。它是一种双组分体系,包括一种硅基化乙烯聚合物(称为接枝共聚物PP 409)和一种含有交联催化剂的母料PP401。这两种材料通常以95份接枝率与5份催化剂母粒的比例使用。 A silane grafted Crosslinkable polyethylene compound, curable by exposure to moisture, for insulation of power cables and possessing excellent extrudability at high output rate. PP 409 has been specially developed for cables up to 72 KV. The special formulation and compounding techniques used ensures that the contamination level is kept within the required limits for this voltage grade. PP 409 has general melt index range of 0.7 - 1.0 which provides firm stability during extrusion, especially for the thick insulations required for high voltage. DESCRIPTION : This compound utilizes the system for crosslinking of polyethylenes developed by DOW coming and known as sioplas. It is a two-component system comprising a silylated ethylene polymer known as the graft copolymer PP 409, and a masterbatch PP401 containing a crosslinking catalyst. The two materials normally used in the ratio of 95 parts graft to 5 parts catalyst masterbatch. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.925 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.75 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
14.5 | MPa | IEC 60811 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
400 | % | IEC 60811 |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
|||
135℃,168 hr 135℃,168 hr |
15 | % | IEC 60811 |
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air |
|||
135℃,168 hr 135℃,168 hr |
% | IEC 60811 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固性 thermosetting 1 |
IEC 60811 | ||
负荷下伸长率:200℃ Elongation under load: 200 ℃ |
% | IEC 60811 | |
冷却后最大永久伸长率:200℃ Maximum permanent elongation after cooling: 200 ℃ |
% | IEC 60811 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
20 ℃ 20 ℃ |
ohms·cm | IEC 60502 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
IEC 60250 | ||
功率因数 power factor 2 |
|||
23℃ 23℃ 2 |
IEC 250 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 15 min, 0.2 N/mm² |
3 50 Hz |
【新闻资讯】查看全部
英力士推出AI优化技术以减排
2021-12-19 搜料网资讯: 近日,英力士宣布,该公司计划在其位于格兰杰默斯的金内尔终端部署创新人工智能驱动的优化技术,将进一步减少其运营中的碳排放。 这一决定是在英力士宣布承诺到 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |