牌号简介 About |
---|
它是热塑性弹性体(TPE)系列中的一种软质、可着色、非吸湿性热塑性硫化弹性 体(TPV)。这种材料同时具有良好的物理性质和耐化学性,用于较难注塑成型的 领域。这一牌号的山都平 TPV 是剪切速率依赖型产品,可在常规热塑性注塑成型 或吹塑成型设备上加工。这是一种聚烯烃基材料,可在生产过程中进行回收利用。 A soft, colorable, non-hygroscopic thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in difficult injection molding applications. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding or blow molding. It is polyolefin based and recyclable within the manufacturing stream. |
产品描述 Product Description
厂家:美国塞拉尼斯 Celanese
类别:TPV
用途:手机;柔软的把手;汽车领域的应用;密封件;消费品应用领域;
颜色:自然色
加工条件:挤出吹塑成型,多次注射成型,注吹成型 Multiple injection molding,Injection Molding
性能特点: 可回收; 防火阻燃等级HB; 尺寸稳定性好; 着色性好; 吸水率低; 柔软性好; 耐化学性; 可清洁; 流动性高; 耐臭氧; 低摩擦系数; 易加工; Good coloring,Ozone resistance,Renewable resources,Low coefficient of friction,Excellent Processability,Good Dimensional Stability,HB,Clean,Low or no water absorption,High liquidity,Soft,Solvent resistance
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.928 | g/cm³ | ASTM D792 |
密度 Density |
0.930 | g/cm³ | ISO 1183 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
5.50 | MPa | ISO 37 |
TD,断裂,23℃ TD, fracture, 23 ℃ |
5.50 | MPa | ASTM D412 |
TD,100% 应变,23℃ TD, 100% strain, 23 ℃ |
2.50 | MPa | ISO 37 |
TD,100% 应变,23℃ TD, 100% strain, 23 ℃ |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
% | ASTM D412 | |
TD,断裂,23℃ TD, fracture, 23 ℃ |
% | ISO 37 | |
压缩形变 Compression deformation |
ASTM D395B | ||
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
125℃,70 hr 125℃,70 hr |
% | ASTM D395B | |
压缩形变 Compression deformation |
ISO 815 | ||
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,15 秒,23℃ Shore A, 15 seconds, 23 ℃ |
ISO 868 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
脆化温度 Embrittlement temperature |
℃ | ISO 812 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
1.1 mm 1.1 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
|||
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
|||
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
Change in Tensile Strain at Break in Air(150℃,168 hr) Change in Tensile Strain at Break in Air(150℃,168 hr) |
% | ISO 188 | |
Change in Durometer Hardness in Air(邵氏 A,150℃,168 hr) Change in Durometer Hardness in Air (150 ℃, 168 hr) |
ASTM D573 | ||
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
|||
邵氏 A,150℃,168 hr Shaw A, 150 ℃, 168 hr |
ISO 188 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.10 mm 1.10 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1 |
3 类型 A |
【新闻资讯】查看全部
又一技术打破国外垄断,东岳ETFE树脂完成国产化
2019-06-24 6月中旬,从东岳集团了解到,该集团完成的乙烯四氟乙烯共聚树脂(ETFE)开发项目在山东淄博通过了由中国石油和化学工业联合会组织的科技成果鉴定。鉴定专家组一致认为,该项目开发 |
又一技术打破国外垄断,东岳ETFE树脂完成国产化
6月中旬,从东岳集团了解到,该集团完成的乙烯—四氟乙烯共聚树脂(ETFE)开发项目在山东淄博通过了由中国石油和化学工业联合会组织的科技成果鉴定。鉴定专家组一致认为,该项目开发的ETFE树脂已实现国产化应用,形成了DS405、DS4051和DS406三个系列产品,生产技术达到国际先进水平,建议进一步加快产品的大规模生产及应用技术开发。
该项目鉴定专家组由中国科学院院士、北京化工大学杨万泰教授,清华大学郭宝华教授,中国氯碱工业协会张文雷秘书长等7位专家组成。
ETFE项目是在2007年12月14日,由原石化协会(现石化联合会)召集国内包括东岳集团在内的氟化工优势企业部署开展的一个攻关项目,也称“12·14”项目。以东岳集团首席科学家张永明教授领衔的含氟功能膜材料国家重点实验室科研团队,系统开展了ETFE树脂的自主开发工作。
历经10余年研发,科研团队先后开发了6代制备工艺技术,并率先掌握了ETFE树脂核心制备技术。采用该项技术,东岳在2016年建设了ETFE树脂标准化中试生产装备,并实现了连续稳定化生产,产品综合性能媲美国外同行产品。
ETFE生产技术最早由美国杜邦公司历经30年研发而成,并在上世纪70年代实现商业化应用,曾一度仅由杜邦、大金等国外公司所掌握。我国科学家从上世纪70年代开始研发该技术,但一直未取得实质性进展,国内所需的ETFE树脂产品100%依赖进口。而且国外对我国军工国防及大飞机领域所需的特种ETFE树脂实施禁运,导致ETFE树脂成为制约我国特殊领域应用和发展的重要瓶颈。
ETFE是继聚四氟乙烯(PTFE)和聚全氟乙丙烯(FEP)后开发的第三大氟树脂品种,同时具有PTFE树脂的耐温、耐介质、耐老化性能和FEP的可热塑性加工特性,是重要的高附加值含氟聚合物,在线缆绝缘、薄膜建筑、化工防腐、新能源、军工国防等领域。
更多行业动态,可关注搜料网。此外,搜料网现有PAI、PC、PA、PEEK材料等工程塑料交流群,包括比利时索尔维、日本东丽、日本三菱、德国道默、韩国乐天、深圳邦克尔塑料等企业均已加入。欢迎产业链上下游的朋友入群探讨,共谋进步。
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。