| 牌号简介 About |
|---|
| XIRAN® SG240是基于SMA（苯乙烯-马来酸酐）的注射成型化合物，具有：高热稳定性、高尺寸稳定性、优异的表面粘合性能。XIRAN® SG240有标准黑色（B）和天然黑色（N）两种颜色。应用领域XIRAN® SG240是一种20%玻璃填充注射成型化合物，设计用于高刚度强度应用。这些产品非常适用于喷涂和发泡零件、耐高温和高丸到丸一致性的精密零件。 XIRAN ® SG240 are styrene maleic anhydride (SMA) based injection molding compounds with: high thermal stability high dimensional stability excellent surface adhesion properties XIRAN ® SG240 is available in standard black (B) and in a natural version (N). XIRAN ® SG240 (B,N) XIRAN ® SG240 is a 20% glass filled injection molding compound designed for applications with high stiffness-strength. These products are very suitable for painted and foamed parts, high temperature resistance and precision parts with high shot to shot consistency. |
产品描述 Product Description
用途：泡沫;高温应用;
颜色：自然色,黑色
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 发泡性好; 机械强度好; 热稳定性好; 尺寸稳定性好; 可表面喷涂; 粘结性好; Good Rigidity,Good Dimensional Stability,Foaming performance,Sprayable,Good bond,Heat Stabilized,HB
填料：玻璃纤维 20
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.20 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
240℃，10.0kg 240℃，10.0kg |
9.0 | g/10min | ISO 1133 |
|
螺旋流动长度 Spiral flow length 2 |
26.0 | cm | Internal Method |
|
收缩率 Shrinkage rate 3 |
Internal Method | ||
|
TD TD |
0.61 | % | 内部方法 |
|
MD MD |
0.25 | % | 内部方法 |
|
吸水率 Water absorption rate |
|||
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ASTM D570 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-40℃ -40℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
|
-40℃ -40℃ |
kJ/m² | ISO 179/1eU | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
|
-40℃ -40℃ |
kJ/m² | ISO 180-A | |
|
23℃ 23℃ |
kJ/m² | ISO 180-A | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/B | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD：-30~80℃ TD：-30~80℃ |
1/℃ | ASTM D696 | |
|
MD：-30~80℃ MD：-30~80℃ |
1/℃ | ASTM D696 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 2 mm |
| 3 Measured according to the Autodesk Mold flow Plastics Labs using a tag mold. |
|
【新闻资讯】查看全部 
南浦环保与全球吉林关于合作事宜停止座谈
2018-12-25 2018年12月13日，南浦集团董事长秦新伟在集团总部会客室会见中国寰球吉林公司党委书记朴龙焕、副总经理张军、市场部部长孙旭、安全质量环保部副部长张艳博一行，双方就南浦环保科技有限公司丙烷-聚丙烯酰胺产业链项目相关合作事宜进行座谈。南浦环保科技总经理张文奎、集团融资部总经理李洪、南浦环保科技副总经理熊伟、法律顾问何溢、集团财务总监等参加会议。 会上，南浦集团董事长秦新伟、中国寰球吉林公司党委书记朴龙焕分别介绍了各自企业的历史 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付