牌号简介 About |
---|
LL1209AA和LL1209KJ是以丁烯-1为共聚单体的线性低密度聚乙烯共聚物。LL1209AA和LL1209KJ适用于共挤吹塑薄膜,具有以下优点:改善热粘。良好的光学性能。低凝胶水平和低气味。良好的基底附着性。坚固的核心层。LL1209AA和LL1209KJ的典型应用是层压膜和热密封层。此外,强烈推荐LL1209KJ用于显示器包装。LL1209KJ提供高滑膜,在厚度范围为35-100微米的纯材料中使用时,易于打开。添加其他聚合物、母料和颜料或使用其他厚度可能会改变薄膜滑动和防堵塞性能。挤出的推荐熔融温度约为180°C-225°C。LL1209AA和LL1209KJ应储存在50°C以下的干燥条件下,避免阳光直射。*LL1209AA和LL1209KJ适用于食品接触。 LL1209AA & LL1209KJ are linear low density polyethylene copolymers containing butene-1 as a co-monomer. LL1209AA & LL1209KJ are suitable for co extrusion blown films with the following advantages: Improved hot-tack. Good optical properties. Low gel level and low odour. Good substrate adhesion. Tough core layer. Typical applications for LL1209AA & LL1209KJ are lamination films and heat sealing layers. Also LL1209KJ is highly recommended for display packaging. LL1209KJ offers high slip film with easy opening properties when used pure in thickness range 35-100 microns. Addition of other polymers, master batches and pigments or use of other thickness may alter film slip and anti-block performance. Recommended melt temperature for extrusion is about 180°C-225°C. LL1209AA & LL1209KJ should be stored in the dry condition below the 50°C and avoided from the exposure of direct sunlight. * LL1209AA & LL1209KJ are suitable for food contact. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.920 | g/cm³ | ASTM D2838 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.90 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
38 | µm | |
薄膜厚度 film thickness |
35 to 100µm | ||
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
9.50 | MPa | ASTM D882 |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
MD,断裂 MD, fracture |
MPa | ASTM D882 | |
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:25 µm MD:25 µm |
g | ASTM D1922 | |
TD:25 µm TD:25 µm |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45° 45° |
ASTM D2457 | ||
雾度 Haze |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
单环管工艺聚丙烯装置聚合催化剂应用研究
2021-08-16 搜料网资讯: 蒲城清洁能源化工有限责任公司成立于2008年11月,由陕西煤业化工集团和中国长江三峡集团共同出资设立。 一期180万t/a甲醇、70万t/a聚烯烃项目以长焰煤为原料,采用了美 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |