牌号简介 About |
---|
Capran® 512 LL是一种热稳定吹塑薄膜,由低内酰胺尼龙6树脂制成。在柔软性和可加工性至关重要的高级复合材料制造和其他高温应用中,建议将其作为袋装薄膜。Capran® 512 LL具有优异的热稳定性和抗针孔。它可以在最高390°F(199°C)的温度下用于典型的复合固化循环时间。 Capran® 512 LL is a heat-stabilized blown film produced from low lactam nylon-6 resin. It is recommended as bagging film for advanced composite fabrication and other high temperature applications where softness and workability are essential. Capran® 512 LL has excellent heat stability and resistance to pinholing. It can be used at temperatures up to 390°F (199°C) for typical composite cure cycle times. |
技术参数 Technical Data | |||
---|---|---|---|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
51 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
31.0 | MPa | ASTM D882 |
MD,断裂 MD, fracture |
112 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
|||
MD,断裂 MD, fracture |
380 | % | ASTM D882 |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD MD |
130 | g | ASTM D1922 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
结晶峰温度 Crystallization peak temperature |
|||
DSC DSC |
℃ | ASTM D3418 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
阿科玛丙烯酸工厂片面晋级
2017-01-13 法国化工巨头阿科玛于日前宣布:将投资9000万美元用于集团德克萨斯州克利尔莱克丙烯酸工厂的设备升级与现代化改造。 作为阿科玛运行升级计划的一部分,集团将以一台全新的90000吨丙烯酸反应釜替换下厂内即将寿终正寝的两台45000吨反应釜。此外,工厂在技术工艺等相关方面也将有所改进。 据悉,新装置预计将于2019年中旬正式投产。届时,克利尔莱克工厂的丙烯酸年产能将达到27万吨。 阿科玛在最新发布的一篇新闻稿中指出:“继集团于2012年至2014年 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |