| 牌号简介 About |
|---|
| Fortron® 1130L4是一种30%的玻璃纤维增强聚苯硫醚，具有优异的耐热性和耐化学性。它本身具有阻燃性，硬度高，强度和刚度平衡良好。特别适用于需要较长流动长度的薄壁零件。由于填料含量低，该等级在二次操作中也表现出良好的可焊性。 Fortron 1130L4 is a 30% glass-reinforced PPS that has excellent heat and chemical resistance. It is inherently flame-retardant and exhibits high hardness and a good balance of strength and stiffness. Especially used for thin walled parts requiring long flow lengths. This grade also exhibits excellent weldability in secondary operations due to its low filler content. |
产品描述 Product Description
用途：薄壁部件;
性能特点： 防火阻燃等级V-0; 机械强度好; 焊接; 耐化学性; 耐高温; 硬度高; 阻燃; Good Rigidity,Good Hardness,Flame Characteristics,High Heat Resistance,Solvent resistance,Welding,V-0
填料：玻璃纤维 30
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.60 | g/cm³ | ASTM D792 |
|
特定体积 Specific volume |
0.636 | cm³/g | ASTM D792 |
|
密度 Density |
1.58 | g/cm³ | ISO 1183 |
|
收缩率 Shrinkage rate |
ISO 294-4 | ||
|
TD TD |
0.60 to 0.90 | % | ASTM D955 |
|
MD MD |
0.30 to 0.50 | % | ASTM D955 |
|
TD TD |
% | ISO 294-4 | |
|
MD MD |
% | ISO 294-4 | |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
% | ISO 62 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
|
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
|
玻璃化转变温度 Glass transition temperature 3 |
℃ | ISO 11357-2 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD TD |
1/℃ | ISO 11359-2 | |
|
MD MD |
1/℃ | ISO 11359-2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
1 kHz 1 kHz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耐电弧性 Arc resistance |
sec | ASTM D495 | |
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | ASTM D3638 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
0.80 mm 0.80 mm |
UL 94 | ||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Specimen Thickness（Shrinkage） Specimen Thickness（Shrinkage） |
mm | Internal Method | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A/1 | |
|
拉伸强度 tensile strength |
|||
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
|
断裂 fracture |
MPa | ISO 527-2/1A/5 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
|
断裂 fracture |
% | ISO 527-2/1A/5 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
弯曲强度 bending strength 2 |
MPa | ISO 178 | |
|
洛氏硬度 Rockwell hardness |
|||
|
M 级 M-level |
ASTM D785 | ||
|
M 级 M-level |
ISO 2039-2 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Break |
| 3 10°C/min |
|
【新闻资讯】查看全部 
跨国企业依然看好中国市场发展前景，持有坚定信心
2022-05-30 近日，世界500强企业巴斯夫护理化学品(上海)有限公司高端护肤靓妆产品技改项目进行了云签约， 总投资约2.8亿元；总投资553.62亿元的巴斯夫一体化基地(广东)有限公司一体化项目也通 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |