牌号简介 About |
---|
EMERGE™ PC 8430-6高级树脂是一种透明的阻燃PC树脂,不含氯化、溴化或磷基添加剂。树脂设计符合德国标准DIN VDE-0472/第815部分关于卤素的要求。这种树脂具有良好的机械和高热性能。EMERGE™ PC 8430-6含有释放剂,且紫外线稳定。Emerge PC 8430-6具有1.8 mm的UL 94 V-0额定值和0.75 mm的UL 94 V-2额定值。应用挤压型材。注塑吹塑制品。照明。 EMERGE™ PC 8430-6 advanced resin is a transparent, ignition resistant PC resin that contains no chlorinated or brominated or phosphorous based additives. The resin is designed to meet the German norm DIN VDE-0472/Part 815 on halogens. This resin combines good mechanical and high heat properties. EMERGE™ PC 8430-6 contains release agent and is UV-stabilized. EMERGE ™ PC 8430-6 has a UL 94 V-0 rating at 1.8 mm and a UL 94 V-2 rating at 0.75 mm. Applications Extruded profile articles. Injection blow moulded articles. Lighting. |
产品描述 Product Description
厂家:美国盛禧奥 Trinseo
类别:PC Polycarbonate
用途:照明应用;
颜色:清晰/透明
加工条件:注吹成型
性能特点: 无卤; 防火阻燃等级V-0; 防火阻燃等级V-2; 耐高温; 阻燃; 耐候抗UV; Weather resistance is good,Halogen free,Flame Characteristics,High Heat Resistance,V-2,V-0
紫外线:UV Stabilized
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ISO 1183/B |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
6.0 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
0.50 到 0.70 | % | ISO 294-4 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
2400 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
ISO 527-2 | ||
屈服 yield |
60.0 | MPa | ISO 527-2 |
断裂 fracture |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
ISO 527-2 | ||
屈服 yield |
% | ISO 527-2 | |
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
球压温度 Ball pressure temperature |
℃ | IEC 60335-1 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
IEC 60250 | ||
1 Hz 1 Hz |
IEC 60250 | ||
50 Hz 50 Hz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
1 Hz 1 Hz |
IEC 60250 | ||
50 Hz 50 Hz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.75 mm 0.75 mm 3 |
UL 94 | ||
1.50 mm 1.50 mm 4 |
UL 94 | ||
1.80 mm 1.80 mm |
UL 94 | ||
3.00 mm 3.00 mm 4 |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
1.0 mm 1.0 mm 3 |
℃ | IEC 60695-2-12 | |
2.0 mm 2.0 mm 4 |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm 4 |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire 4 |
IEC 60695-2-13 | ||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index 4 |
% | ISO 4589-2 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance 5 |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
3 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
4 standard tints |
【新闻资讯】查看全部
铃木新车前格栅由三菱化学生物基塑料制成
2022-06-10 三菱化学控股集团(MCHG)宣布,其生物基工程塑料DURABIO已用于铃木汽车公司新型S-CROSS前格栅的生产。 据搜料网了解,DURABIO由可再生植物中的异山梨醇制成,是一种生物基工程塑料。 |
铃木新车前格栅由三菱化学生物基塑料制成
三菱化学控股集团(MCHG)宣布,其生物基工程塑料DURABIO已用于铃木汽车公司新型S-CROSS前格栅的生产。
据搜料网了解,DURABIO由可再生植物中的异山梨醇制成,是一种生物基工程塑料。相较于传统工程塑料,它提供很好的性能优势,如抗冲击性、耐候性和耐热性。
生物基工程塑料DURABIO还具有良好的显色性,只需添加着色剂即可达到高光泽和精美的设计。
此外,由于这种塑料的表面坚硬且耐刮擦,因此不需要涂漆和涂层工艺,从而减少了生产过程中的VOC排放。
此前,铃木已将DURABIO应用于内饰零件。由于对外饰零件的抗震性和耐候性要求很高,经过多次实验调整后,这种材料首次用于铃木外饰零件。
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。