| 牌号简介 About |
|---|
| LLBF-120A是一种具有丁烯共聚单体的经认证的主要树脂，设计用于生产一般用途包装中使用的吹塑薄膜。LLBF-120A具有工艺性好、薄膜强度好、热封温度范围宽等优点。LLBF-120A的应用包括服装袋，生产袋和衬里。LLBF-120A不含滑动和防堵。LLBF-120A符合FDA法规21CFR 177.1520（c）3.1a和大多数有关在食品接触中使用聚乙烯的国际法规。 LLBF-120A is a certified prime resin with Butene-comonomer, designed for production of Blown films used in general purpose packaging. LLBF-120A features excellent combination of easy processability with good film strength as well as wide heat sealing temperature range. LLBF-120A applications include garment bags, produce bags and liners. LLBF-120A contains no slip and no antiblock. LLBF-120A complies with FDA regulation 21CFR 177.1520(c)3.1a and with most international regulations concerning the use of Polyethylene in contact with food articles. |
产品描述 Product Description
用途：薄膜;袋子;洗衣袋;
加工条件：吹塑薄膜
性能特点： 机械强度好; 丁烯共聚单体; 食品接触; 密封范围宽; 易加工; Good Rigidity,Excellent Processability,Food contact compliance,Broad Seal Range,Butylene copolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.920 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
1.0 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
25 | µm | |
|
割线模量 Secant modulus |
|||
|
1% 正割，TD，25 µm，吹塑薄膜 1% secant, TD, 25 µ m, blow molded film |
223 | MPa | ASTM D882 |
|
1% 正割，MD，25 µm，吹塑薄膜 1% secant, MD, 25 µ m, blow molded film |
193 | MPa | ASTM D882 |
|
拉伸强度 tensile strength |
|||
|
TD，断裂，25 µm，吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
|
TD，屈服，25 µm，吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ASTM D882 | |
|
MD，断裂，25 µm，吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
|
MD，屈服，25 µm，吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
|||
|
TD，断裂，25 µm，吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
|
MD，断裂，25 µm，吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
|
落锤冲击 Drop hammer impact 2 |
|||
|
25 µm，吹塑薄膜 25 µ m, blow molded film 2 |
g | ASTM D1709-A | |
|
撕裂强度 tear strength |
|||
|
TD，25 µm，吹塑薄膜 TD, 25 µ m, blow molded film |
g | ASTM D1922 | |
|
MD，25 µm，吹塑薄膜 MD, 25 µ m, blow molded film |
g | ASTM D1922 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，25.4 µm，吹塑薄膜 45 °, 25.4 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
25.4 µm，吹塑薄膜 25.4 µ m, blow molded film |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 F50 |
|
【新闻资讯】查看全部 
投资10亿元！长兴集团新建年产19.7万吨环氧树脂/丙烯酸树脂等项目
2022-02-10 近日，铜陵经济技术开发区发布了长兴材料工业(铜陵)有限公司年产19.7万吨合成树脂项目环评公示。 长兴集团旗下全资子公司长兴材料工业(铜陵)有限公司计划总投资10.35亿元新建年产 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付