牌号简介 About |
---|
TENITE纤维素塑料以其优良的性能平衡而闻名——韧性、硬度、强度、表面光泽、透明度和温暖感。细纤维素塑料的力学性能随增塑剂用量的不同而不同。增塑剂含量越低,表面越硬,耐热性越高,刚性越高,拉伸强度越高,尺寸稳定性越好。增塑剂含量越高,冲击强度越高。Tenite纤维素塑料有天然、透明、精选的橱柜或烟雾透明和黑色半透明。颜色浓缩物可按10:1到40:1的比例稀释。醋酸丁酸纤维素酯530-10含有防臭面具,增塑剂含量为10%。 Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulosic plastics are available in natural, clear, selected ambers, or smoke transparents and black translucent. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite™ Cellulose Acetate Butyrate 530-10 contains an odor mask and has a plasticizer level of 10%. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.19 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.20 到 0.60 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
1.4 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-40℃ -40℃ |
96 | J/m | ASTM D256 |
23℃ 23℃ |
240 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 2 |
ASTM D648 | ||
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp 2 |
℃ | ASTM D1525 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23℃ MD:23℃ |
1/℃ | ASTM D696 | |
比热 specific heat |
|||
23℃ 23℃ |
J/kg/℃ | DSC | |
导热系数 Thermal conductivity coefficient 3 |
|||
23℃ 23℃ 3 |
W/m/K | ASTM C177 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
|||
23℃ 23℃ |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
23 ℃,1 MHz 23 ℃,1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
23℃,1 MHz 23℃,1 MHz |
ASTM D150 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Transmittance |
|||
1520 µm 1520 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
1520 µm 1520 µm |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
可溶性物质损失 Loss of soluble substances |
|||
23℃ 23℃ |
% | ASTM D570 | |
加热减量 Heating reduction |
|||
72 hrs,80℃ 72 hrs,80℃ |
% | ASTM D707 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength |
ASTM D638 | ||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Conditioned 4 hours at 70°C (158°F) |
3 Range: 0.17 to 0.33 |
【新闻资讯】查看全部
我国炼油行业加快升级步伐
2019-02-18 中国石油经济技术研究院最新发布的《2018国内外油气行业发展报告》显示,截至2018年底,我国炼油能力达到8.31亿吨/年。在炼油能力持续增长的同时,我国炼油行业也在加快“由大转强”的升级步伐,无论是三大石油公司全面推进深化改革,还是以恒力石化为代表的大型民营炼厂快速崛起,都在推动我国炼油行业向高质量、差异化和绿色化发展。 三大公司优化结构 中国石油经济技术研究院副院长姜学峰在解读《报告》时表示,作为我国油气行业的主力军,中 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-Tenite™ Butyrate 530E3720010 Clear, Trsp证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)