牌号简介 About |
---|
BMC 605LS成型化合物是一种低收缩、矿物填充、玻璃纤维增强的聚酯化合物,适用于压缩、转移和填充器注射成型,具有良好的可塑性、中等冲击强度和优异的整体电气性能和阻燃性。典型应用包括断路器、变压器线轴和电机端盖。BMC 605LS模塑料是在工业颜色范围内以挤压形式生产的。其长度可达12英寸的原木或特定重量的预切段塞,直径为1“至2½米。在这个范围内,较小的直径作为多次挤压提供;重量公差为正负5%,最大正负15克。 BMC 605LS molding compound is a low-shrink, mineral filled, glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding It is characterized by good moldability, medium impact strength and excellent overall electrical properties and flame resistance. Typical applications include circuit breakers, transformer bobbins and motor end bells. BMC 605LS molding compound is produced in extruded form in a range on industrial colors. It is available in logs up to 12 inches in length or as precut slugs, of specific weight, in dia meters from 1" to 2 ½" . Within this range, smaller diameters are supplied as multiple extrusion; and weight tolerances are plus or minus 5 %, up to a maximum of plus or minus 15 grams. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.88 to 1.96 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.10 to 0.22 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.14 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
模压成型 Compression Molding |
110 to 320 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
> 260 | ℃ | ASTM D648 |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength 2 |
kV/mm | ASTM D149 | |
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
6.40 mm 6.40 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,模压成型 Yield, molding |
MPa | ASTM D638 | |
弯曲强度 bending strength |
|||
模压成型 Compression Molding |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
巴氏硬度 Babbitt hardness 2 |
ASTM D2583 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法A(短时间) |
【新闻资讯】查看全部
索尔维PEEK初次用于基因学研讨
2016-05-06 全球最大的基因组织华大基因(BGI)近日宣布已经选择索尔维特种聚合物公司的KetaSpire聚醚醚酮(PEEK)用于新一代排序平台BGISEQ-500。 索尔维PEEK首次用 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |