Lupoy PC 1302UV-08树脂专为挤出和注塑产品设计。它在耐热性、透明度和冲击强度方面表现出良好的物理性能平衡。 LUPOY PC 1302UV-08 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength. |
产品描述 Product Description
厂家:韩国LG化学 LG Chemical
类别:PC Polycarbonate
用途:镜头;眼镜;电器用具;
加工条件:注射成型 Injection Molding
性能特点: 高粘度; 防火阻燃等级V-2; 耐高温; 透光性好; 冲击性能好; Good Clarity,High impact resistance,High Viscosity,High Heat Resistance,V-2
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
8.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 到 0.70 | % | ASTM D955 |
吸水率 Water absorption rate |
ASTM D570 | ||
23℃,24hr 23℃,24hr |
0.15 | % | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.32 | % | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 2 |
|||
23℃,3.2mm 23℃,3.2mm 2 |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
ASTM D256 | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 3 |
|||
23℃,3.20 mm,Total Energy 23℃,3.20 mm,Total Energy 3 |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,退火,4.0 mm 0.45 MPa, annealed, 4.0 mm |
℃ | ||
1.8 MPa,未退火,4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ||
1.8 MPa,退火,4.0 mm 1.8 MPa, annealed, 4.0 mm |
℃ | ||
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
球压温度 Ball pressure temperature |
℃ | IEC 60598-1 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~82℃ MD:-40~82℃ |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
60 Hz 60 Hz |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
2.00 mm 2.00 mm |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.50 mm 0.50 mm |
|||
1.60 mm 1.60 mm |
|||
2.50 mm 2.50 mm |
|||
3.00 mm 3.00 mm |
|||
灼热丝起燃温度 Igniting temperature of the hot wire 5 |
|||
2 mm 2 mm 5 |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
平均燃烧程度 Average combustion degree |
cm | ASTM D635 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
|||
R 级 R-level |
|||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
MPa | ||
断裂 fracture |
MPa | ||
拉伸应变 Tensile strain |
ASTM D638 | ||
屈服 yield |
% | ||
断裂 fracture |
% | ||
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
耐磨耗性 Wear resistance 1 |
|||
Change in Haze Change in Haze 1 |
% | ASTM D1004 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 1000g, 500 cycles, CS-10F Wheel |
3 9.8 mil 缺口深度 |
4 11.1 ft/sec |
5 速率 A (50°C/h), 载荷2 (50N) |
6 5 sec |
【新闻资讯】查看全部
普勒特推出Somos Perfoamer物理塑料发泡零碎
2018-10-30 普勒特高分子工艺技术有限公司(德国,本斯海姆)上周在德国腓特烈港的Fakuma塑料工业展览会上推出Somos Perfoamer物理塑料发泡系统。该系统包括调节和浸渍单元,在将粒料进行处 |
普勒特推出Somos Perfoamer物理塑料发泡零碎 普勒特高分子工艺技术有限公司(德国,本斯海姆)上周在德国腓特烈港的Fakuma塑料工业展览会上推出Somos Perfoamer物理塑料发泡系统。该系统包括调节和浸渍单元,在将粒料进行处理后,直接送入注塑机内。项目和加工领域的高级技术专家Hans Schnell说:“Perfoamer系统的研制成功,使得塑料加工商在工业规模上具备了Plastinum泡沫注塑成型工艺优势,这套工艺是由Linde和Kunstoff-InstitutLüdenscheid联合开发的。” 将聚合物粒料干燥,并在调节单元中保持于最佳加工温度,然后在相邻的高压釜中用CO2浸渍。与工业4.0项目良好兼容的PLC控制系统可以确保过程质量的一致性。将掺杂CO2的粒料存储在一个250升的罐中,之后将被输送到注塑成型机中。Perfoamer系统几乎可以与所有的注塑机兼容。 Plastinum泡沫注塑成型技术(基础版)的开发是为了兼具物理、化学发泡的优点。Linde表示:“该技术安装简单,几乎不需要对注塑设备进行任何改造,而且其成本比传统的物理发泡系统低60%。” 包括生物基和工程级材料、纯敏感热塑性塑料、复合材料在内的大多数聚合物,均可由Somos Perfoamer系统加工制成。据ProTec称,发泡可以减轻材料的重量高达60%,但具体情况还取决于材料的种类。该公司补充说:“此外,二氧化碳含量的升高将会导致聚合物粘度的降低,从而改善了熔体流动性,提高了生产效率。” ProTec 聚合物加工工艺将为塑料加工公司提供材料处理和回收技术以及LFT拉挤生产线。 来源:材料科技在线 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- 汽车转向灯外壳
- 2019-06-25 0
- Lupoy® 3030-10是注塑成型的聚碳酸酯树脂。它在耐热性、透明度和冲击强度方面表现出良好的物理性能平衡。
- 阅读全文
汽车转向灯外壳
收起
抱歉!暂无数据。