Jampilen HP554P是一种高流动性聚丙烯均聚物,用于生产细旦短纤维,提高了非织造布的热粘合能力。该产品具有良好的抗气体褪色性能。Jampilen HP552在短纺纱线和一些特定的长纺纱线上具有出色的工艺稳定性和纺纱性能。热粘合能力强,可生产撕裂强度较高或每平方米重量较低的同等强度非织造布。以果酱HP552R为原料制成的织物具有柔软、织物外观、抗撕裂等特点。典型的应用是尿布、女性护理产品、热粘合非织造布和尿失禁垫的积压。其他应用包括用于服装和家具行业的抹布、过滤器和织物。 "Jampilen HP554P" is a high Fluidity polypropylene homopolymer for the production of fine denier staple fiber with improved thenno-bonding ability for nonwoven fabrics. The product exhibits excellent antigasfading properties. "Jampilen HP554P" offers outstanding process stability and spinning behavior on short-spinning lines and some specific long-spinning lines. The thermal-bonding ability is high and allows the production of nonwoven fabrics with higher tear strength or with lower weight per square meter for the same strength. The fabrics made with "Jampilen HP554P" are characterized by softness, textile-like appearance and high tear resistance. The typical applications are overstock for diapers, feminine care products, thermal-bonded nonwovens and incontinence pads. Other applications are wipes, filters and fabrics for the clothing and fumiture industry. Features: Good spinnability High thermobonding properties Excellent antigasfading properties High tear resistance Good heat seal Homopolymer Typical Applications: Nonwoven staple fibers Overstock for diapers Feminine care products Incontinence pads Filters and fabrics for the clothing and fumiture industry Fine denier filaments for Carpet face yam Multifilament yams |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
18 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
30 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
95.0 | ℃ | ASTM D648 |
维卡软化温度 Vicat Softening Temp |
154 | ℃ | ASTM D1525 2 |
加速干燥箱老化 Accelerate oven aging |
|||
150℃ 150℃ |
hr | ASTM D3012 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 压 力1 (10N) |
【新闻资讯】查看全部
促力可持续发展 埃万特推出NymaxBIO低吸水率和生物基聚酰胺配方
2022-03-17 3月16日,埃万特推出全新Nymax BIO配方。据悉,这是一种生物基聚酰胺系列材料,可帮助解决市面上许多生物源聚酰胺材料的吸水率不能满足要求的难题。 (图片来源于埃万特) Nymax B |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |