牌号简介 About |
---|
它是热塑性弹性体(TPE)系列中的一种软质、黑色、特种非吸湿性热塑性硫化弹 性体(TPV)。它专门配制用于与 ABS、PS、PC、PMMA、ASA、PET 和 PPO/PS 共混 物粘结,适合于要求硬/软材料组合的应用。这一牌号的山都平 TPV 是剪切速率依 赖型产品,可在常规热塑性注塑成型或挤出成型设备上加工。这是一种聚烯烃基材 料,可在生产过程中进行回收利用。 A soft, black, specialty, non-hygroscopic thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. It is especially formulated to bond to ABS, PS, PC, PMMA, ASA, PET and PPO/PS blends for applications where hard/soft combinations are required. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding or extrusion. It is polyolefin based and recyclable within the manufacturing stream. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ASTM D792 |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸应变 Tensile strain |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
600 | % | ISO 37 |
TD,断裂,23℃ TD, fracture, 23 ℃ |
600 | % | ASTM D412 |
压缩形变 Compression deformation |
|||
125℃,70 hr 125℃,70 hr |
55 | % | ISO 815 |
125℃,70 hr 125℃,70 hr |
% | ASTM D395B | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,15 秒,23℃ Shore A, 15 seconds, 23 ℃ |
ISO 868 | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ASTM D573 | ||
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
125℃,168 hr 125℃,168 hr |
% | ASTM D573 | |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ISO 188 | ||
100℃,168 hr 100℃,168 hr |
% | ISO 188 | |
125℃,168 hr 125℃,168 hr |
% | ISO 188 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
ASTM D573 | ||
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
125℃,168 hr 125℃,168 hr |
% | ASTM D573 | |
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air |
ISO 188 | ||
100℃,168 hr 100℃,168 hr |
% | ISO 188 | |
125℃,168 hr 125℃,168 hr |
% | ISO 188 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
ASTM D573 | ||
邵氏 A,100℃,168 hr Shaw A, 100 ℃, 168 hr |
ASTM D573 | ||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr |
ASTM D573 | ||
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
ISO 188 | ||
邵氏 A,100℃,168 hr Shaw A, 100 ℃, 168 hr |
ISO 188 | ||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr |
ISO 188 | ||
拉伸强度的变化率 The rate of change in tensile strength |
ASTM D471 | ||
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ASTM D471 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ASTM D471 | |
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ASTM D471 | |
拉伸强度的变化率 The rate of change in tensile strength |
ISO 1817 | ||
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ISO 1817 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ISO 1817 | |
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ISO 1817 | |
极限伸长率的变化率 Change rate of ultimate elongation |
ASTM D471 | ||
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ASTM D471 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ASTM D471 | |
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ASTM D471 | |
断裂时拉伸应力变化 Changes in tensile stress during fracture |
ISO 1817 | ||
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ISO 1817 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ISO 1817 | |
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ISO 1817 | |
邵氏硬度的变化率 The rate of change in Shore hardness |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在乙醇中,95% Shore A, 23 ℃, 168 hr, in ethanol, 95% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在盐酸中,10% Shore A, 23 ℃, 168 hr, in hydrochloric acid, 10% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在IRM 903 油中 Shaw A, 23 ℃, 168 hr, in IRM 903 oil |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在氢氧化钠中,50% Shore A, 23 ℃, 168 hr, in sodium hydroxide, 50% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在水中 Shaw A, 23 ℃, 168 hr, in water |
ASTM D471 | ||
邵氏硬度的变化率 The rate of change in Shore hardness |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在乙醇中,95% Shore A, 23 ℃, 168 hr, in ethanol, 95% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在盐酸中,10% Shore A, 23 ℃, 168 hr, in hydrochloric acid, 10% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在IRM 903 油中 Shaw A, 23 ℃, 168 hr, in IRM 903 oil |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在氢氧化钠中,50% Shore A, 23 ℃, 168 hr, in sodium hydroxide, 50% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在水中 Shaw A, 23 ℃, 168 hr, in water |
ISO 1817 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.10 mm 1.10 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1 |
3 类型 A |
【新闻资讯】查看全部
石化工程界“一带一路”寻机遇
2017-06-08 6月7日,以“‘一带一路’寻机遇、携手共进谋发展”为主题的首届北京国际工程发展论坛举行。会议认为,在石化行业“走出去”的大潮中,石化工程企业要成为行业抱团出海的核心,走在行业集群“走出去”的前列。 中国石油 |
石化工程界“一带一路”寻机遇 6月7日,以“‘一带一路’寻机会、携手同行谋出路”为主题风格的第一届北京国际工程项目学术研讨会举办。大会觉得,在石油化工行业“走出去”的浪潮中,石油化工工程项目公司要变成领域报团出航的关键,走在领域群集“走出去”的前端。 中国原油和化工协会会生长李寿生表明,促进“一带一路”提倡在中国建设工程行业的执行,针对提升建设工程公司国际性间的协作、加强国际性工程项目项目风险管理、打造出中国国际性一流的工程公司等,都具备关键的实际意义。石油化工类工程公司要充分运用与众不同优点,勤奋变成石油化工行业报团“走出去”的力量训练方法。 中国石油化工勘察设计协会主席荣世立强调,一批中国公司已经向技术性和资本输出超越,应对“一带一路”的发展趋势机遇与挑战,中国公司不可以靠孤军奋战,而应当靠协作共享资源;不可以有骄傲自满观念,应当见到大家存在的不足和差别,要普遍消化吸收国际性大企业的发展趋势工作经验,持续提高自身的整体实力。 据统计,2016年中国对外开放工程承包进行销售额1594.两亿美金,新签订合同额2440.1亿美元,另外中国对外开放对外直接投资猛增至1888亿美金,创下历史时间新纪录。应对中国境外投资的不断发展及其工程项目销售市场的现代化,许多勘察设计公司在发展国际性工程项目销售市场层面也迈开喜人脚步。据调查,2006年至2015年的十年间,中国约170家勘察设计公司进行的国外施工总承包合同书总金额从166亿人民币提升到728亿人民币。 中国勘察设计研究会副会长兼理事长白马王子牛表明,中国勘察设计公司一定要抓住机会,加速现代化脚步,做好发展战略发展趋势精准定位,新项目运行要规范性,重视培养专业人才及营造企业品牌,然后在运营模式、人才结构、规范、信息化管理和风险监管这五个层面与国际性对接。 德国巴斯夫(中国)有限责任公司全世界高级副总裁冯晖共享了海外工程公司新项目运行层面的工作经验。他提议,中国工程公司要在市场定位做好早期市场调研,对本地文化冲突、法律法规规定、政府部门审核、本地香港移民规章、中国海关政策法规等开展详尽的掌握。为减少“走出去”的风险,对在国外实行的新项目必须科学研究新项目所在城市的规定,充足回应法律法规规定的税金,尤其注意代收代缴税、所得税和别的税费。 液化空气亚太地区项目投资实行管理中心高级副总裁韩宗奎建言献策,“走出去”的公司要有一个风险监管精英团队,要留意外界风险、合同书类风险、财产项目投资类风险、技术专业风险和运作类风险。 英美资源集团公司北京市办事处首席总裁及谈判代表付武表明,中国销售市场十分关键,中国要求铸就了上一轮的煤业兴盛,因此中国公司“走出去”要打好中国要求这张牌。 此次社区论坛由中国原油和化工厂勘察设计研究会、中国勘察设计研究会基本建设项目风险管理和施工总承包联合会、韦斯特帕森(中国)企业协同举行,近200名专业人士参会。 来源于:中国化工厂报 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。